Preparation of High Solid Content Polyurethane Emulsion with Sulfonate Hydrophilic Chain-Extending Agents

Xiao Li Wei; Fa Xing Zhang

doi:10.4028/www.scientific.net/AMM.548-549.57

Paper Titles

Pore Size Control of Ordered Mesoporous Carbons and Adsorption Performance of Dye Molecules
p.38

Investigating the Effects of Blending Ratio and Injection Parameters on the Tensile Properties of Glass Fiber-Filled Nylon 66 Composite Gear
p.43

Polycrystalline Silicon Wafer Surface Color Defect Inspection Based on Machine Vision
p.48

Investigation into the Differences Thermal Properties of SLS Polymer Powder Materials Using Differential Scanning Calorimetry (DSC)
p.53

Preparation of High Solid Content Polyurethane Emulsion with Sulfonate Hydrophilic Chain-Extending Agents
p.57

Asbestos and Alternative Materials
p.61

Relationship between Foamability and Nanoparticle Concentration of Carbon Dioxide (CO₂) Foam for Enhanced Oil Recovery (EOR)
p.67

Preparation of Hydroxyapatite Composite Coatings with Interlayer of TiO₂ and its Corrosion Behaviors
p.72

Encapsulation of Multi-Enzymes on Waste Clay Material: Preparation, Characterization and Application for Tapioca Starch Hydrolysis
p.77

HomeApplied Mechanics and MaterialsApplied Mechanics and Materials Vols. 548-549Preparation of High Solid Content Polyurethane...

Preparation of High Solid Content Polyurethane Emulsion with Sulfonate Hydrophilic Chain-Extending Agents

Abstract:

A series of novel stable polyurethane emulsion with high-solid-content and low-viscosity were prepared by self-emulsification. They were prepared by the reaction of poly (tetrahydrofuran-co-oxidation of propylene) glycol (Ng210), isophorone isocyanate (IPDI) with 1,2-dihydroxy-3-propanesulfonic acid salt (DHPA) as hydrophilic chain-extending agents. Influence of the content of DHPA on properties of polyurethane emulsion and film were analyzed .The results show that obtained emulsion were multivariate distribution in particle size and were spherical particles by measurement of grain size and electron microscopic photo. It is noticed that with increasing content of DHPA and, average particles diameter of polyurethane emulsion became smaller, poly-dispersion became narrower and solid-content became bigger. when the content of DHPA is 7%, solide-concent of emulsion reaches 61%. In addition, Polyurethane emulsion are endowed stability of emulsion are good at high temperature and low temperature as well as storage stability.