Effect of Zinc Coating on Mechanical Behavior of Al 7075

Abstract:

The addition of zinc to aluminum with magnesium or copper produces heat treatable alloys of highest strength which can be used for structural applications. This work is an attempt to investigate any improvement in hardness and fracture toughness by coating aluminum 7075 alloy with zinc. The zinc coated aluminum 7075 alloy was fabricated using Time Dependent Electro-Plating Technique. The thickness of the coating is a function of time. The varying thickness of zinc coating was obtained based on the time estimates, which includes 10, 15 and 20 microns. Specimens were prepared according to ASTM standards, which were then tested for mechanical properties such as surface hardness, tensile strength and fracture toughness at different loading conditions. The results, when compared to the uncoated aluminum alloy showed significant improvement in Hardness (87 RHN). The hardness increased slightly compared to that of uncoated surface and showed no increase with the increase in the thickness of coating. The yield stressof zinc coated aluminum alloy increased (587.11 N/mm²) when compared to uncoated aluminum alloy 7075 - T6 (537.12 N/mm²), with an increase in brittleness. The fracture toughness test on CT specimen under plain strain condition for coated specimen showed an increase in K_IC value by 7.25 % compared to that of uncoated aluminum 7075–T6 alloy. Optical microscopy analysis shows that there is a good bonding of zinc coating on aluminum.

• Periodical: Applied Mechanics and Materials (Volumes 592-594)
• Pages: 255-259
• DOI: https://doi.org/10.4028/www.scientific.net/AMM.592-594.255
• Online since: July 2014
• Authors: B.P. Dileep*, V. Ravi Kumar, Mrudula Prashanth, M.V. Phanibhushana
• Keywords: AA7075, Fracture Toughness, Mechanical Property, Zinc Coating

References

[1] American Galvanizers Association, information on web: http: /www. galvanizeit. org.

[2] E. Zalnezhad& Ahmed A. D. Sarhan& M. Hamdi, in : A fuzzy logic based model to predict surface hardness of thin film TiN coating on aerospace AL7075-T6 alloy of Int J Adv Manuf Technol vol. 68 (2013) p.415–423.

DOI: 10.1007/s00170-013-4738-y

[3] R. GhelichiaD. MacDonaldb, S. Bagherifarda, H. Jahedc, M. Guaglianoa, B. Jodoinb in : Microstructure and fatigue behavior of cold spray coated Al5052 of Acta Materialia Volume 60, Issue 19(2012), p.6555–6561.

DOI: 10.1016/j.actamat.2012.08.020

[4] E. Zalnezhad , Ahmed A. D. Sarhan, M. Hamdi in : Optimizing the PVD TiN thin film coatings parameters on aerospace AL7075-T6 alloy for higher coating hardness and adhesion with better tribological properties of the coating surface of Int J AdvManufTechnol (2013).

DOI: 10.1007/s00170-012-4022-6

[5] Sarmed Abdalrasoul Salih, Abdalrasoul Salihh Mehdi Ali Safa Nouri Alsaegh In : Study the Effect of Nickel Coating on Fatigue Life of Low Carbon Steel Exposed to Corrosive Environments of Journal of Environment and Earth Science, www. iiste. org ISSN 2224-3216 (Paper) ISSN 2225-0948 (Online) Vol. 3, No. 5(2013).

[6] E. Zalnezhad, Ahmed A. D. Sarhan, M. Hamdi in : Fretting fatigue life evaluation of multilayer Cr–CrN-coated Al7075-T6 with higher adhesion strength—fuzzy logic approach of Int J Adv Manuf Technol (2013) vol. 69 p.1153 – 1164.

DOI: 10.1007/s00170-013-5093-8

[7] M A. Ramalho, L.M. Correia, J.D. Costa in : Fretting fatigue of zinc coated low carbon steel EN H320 of Tribology International vol. 33 (2000) p.761–768 www. elsevier. com/locate/triboint.

DOI: 10.1016/s0301-679x(00)00119-5

[8] Information on http: /en. wikipedia. org/wiki/7075_aluminium_alloy.