Study on Preparation and Property of Carbon Fiber/HA Composites by Centrifugal Slip Casting Method

Qiang Li; Jing Yuan Yu; Xiu Juan Meng

doi:10.4028/www.scientific.net/AMR.1058.180

Paper Titles

Optical Diagnosis of Atmospheric Pressure Gas-Liquid Diffuse Discharge Excited by Nanosecond Pulse Voltage
p.158

Hot Deformation Behaviors of SiCp/Al Composites
p.165

Preparation and Characterization of SiC/SiC Micro Ceramic Matrix Composites
p.170

Effect of MgO-Y₂O₃ Additions on Microstructure and Mechanical Properties of Al₂O₃-TiCN Composites
p.176

Study on Preparation and Property of Carbon Fiber/HA Composites by Centrifugal Slip Casting Method
p.180

The Preparation, Structure and Electrical Conductivity of Ag-Doped La_1-x-ySr_xCu_yMnO_3-δ (0.05≤x≤0.4, y=0.1) Ceramics
p.185

Effect of Doping Ions on Structure and Electrical Properties of Lead-Free KNN Ceramics
p.190

Densification Mechanism of Antimony-Doped Tin Oxide Ceramics by Spark Plasma Sintering
p.196

Adsorption-Desorption Performances of Humidity Controlling Diatomite-Based Ceramics
p.200

HomeAdvanced Materials ResearchAdvanced Materials Research Vol. 1058Study on Preparation and Property of Carbon...

Study on Preparation and Property of Carbon Fiber/HA Composites by Centrifugal Slip Casting Method

Abstract:

In this paper, centrifugal slip casting method was use to prepare carbon fiber/HA composites using the nanoHA particles and carbon fibers as initial materials. The morphology of the carbon fiber after modification of p-aminobenzoic acid was observed. The rheological characteristic of the carbon fibers/HA slurries was studied. The effects of the centrifugal acceleration on green density uniformity of carbon fiber/HA composites were analyzed. The bending strength and fracture toughness of carbon fiber/HA composites were measured. The results show the roughness of carbon fibers treated by p-aminobenzoic acid increases. At the pH of 10 and 5 wt% dispersant, the HA slurries with 3 vol% carbon fibers have good fluidity. After centrifuged at 2860 G for 30 min, the green compacts of HA composites have high and uniform the green density. After sintered at 1100°C for 1h, compared with carbon fiber/HA composites prepared by dry pressing, the modified carbon fiber/HA composites prepared by centrifugal slip casting have higher bending strength and fracture toughness of 89.4 MPa and 1.92MPa^1/2, respectively.