Study on Crack Bridging Ability of Polymer-Modified Cement Based Compounds for Waterproofing Material

Abstract:

China's existing polymer-modified cement based compounds for waterproofing material standards are used for the tensile strength test and elongation at break test as the test method to evaluate the performance of the product extension. The elongation only reflects the extension ability of product, but cannot indicate the crack bridging ability of the product. In engineering applications, there is a requirement for higher bridging cracks ability of the products. In this paper, 9 samples of polymer-modified cement based compounds for waterproofing material were tested. Crack bridging ability was tested under the standards and methods in DIN EN 14891:2013-07. Tensile strength and elongation at break were tested according to the standards and methods in GB23445:2009. The crack bridging ability test results are between 0 to 2.08mm, in which 5 of them meet the requirements of greater than 0.75mm according to DIN EN14891:2013-07.The tensile strength test results are between 1.13MPa to 3.19MPa, the elongation at break test results are between 4% to 350%.The results show that higher tensile strength and higher elongation at break will have good ability of crack bridging. Samples with better crack bridging ability are close to type III product according to GB23445-2009 which requires tensile strength ≥ 1.8MPa and elongation at break ≥ 30%. Crack bridging ability directly reflects the product’s ability of crack bridging, and is more in line with the actual requirements in engineering applications. It is recommended that the crack bridging ability test method should be adopted in the formulation of China polymer-modified cement compounds for waterproofing material standards.

• Periodical: Advanced Materials Research (Volume 1129)
• Pages: 217-221
• DOI: https://doi.org/10.4028/www.scientific.net/AMR.1129.217
• Online since: November 2015
• Authors: Hong Zhao, Wei Li, Yong Ming Zhang
• Keywords: Crack Bridging Ability, Elongation, Polymer-Modified Cement Based Compounds for Waterproofing Material

References

[1] Xu F, Liu L, Polymer cement-based building materials and applications, China Architecture Industry Publisher, Beijing, 2010. 173-174.

[2] Zhai Y, Yang L, Zhang X, Study on department of acrylic polymer modified cement based waterproof coating, J. China Building Waterproofing, 2012(9), 1-3.

[3] GB/T23445-2009 Polymer-modified Cement based compounds for Waterproofing Material, S. (2009).

[4] DIN EN 14891: 2013-07 Liquid-applied water impermeable products for use beneath ceramic tiling bonded with adhesives –Requirements, test methods, evaluation of conformity, classification and designation. S. (2013).

DOI: 10.3403/30119206

[5] ETAG022 Guideline for European technical approval of watertight covering kits for wet room floors and or walls (Part 3: Kits based on inherently watertight boards), S. (2010).

[6] C 1305 – 08 Standard test method for crack bridging ability of liquid-applied waterproofing membrane. S. (2008).

[7] Deng C. Controversies overtype III product in national standard < Polymer cement waterproofing coatings > and explanation, J. China Building Waterproofing, 2010(14), 1-4.