Complexing Agent on the Surface of Magnesium Alloy Plating of Ni-B Alloy

Abstract:

CPM9V high speed steel(HSS) ring billet was prepared by spray forming(SF), the yield is 83.5%, porosity is 0.8%, spray forming preparation method and technological parameter were illustrated. The microstructure and carbide morphology on the different position of billet were observed. The results show that carbide particles have small size, regular shape and uniform distribution, alloy element without segregation. There are some pores and defects in the position of ring billet closed to deposition substrate, come from spray forming instability beginning stage.

• Periodical: Advanced Materials Research (Volumes 311-313)
• Pages: 327-330
• DOI: https://doi.org/10.4028/www.scientific.net/AMR.311-313.327
• Online since: August 2011
• Authors: Yu Cai, Zhen Zhen Chang, Chun Mei Chen, Yu Ting Bai, Ya Wei Lin, Zhi Qiang Li
• Keywords: Electroless Plating (EP), Magnesium Alloy, Ni-B Alloy and Complexing Agent

References

[1] Riyao Xu: Magnesium metal production technology (Zhongnan university press in Changsha, Changsha 2003).

[2] Maozhong An: Electroplating theory and technology (Harbin industrial university press in Harbin, Harbin 2004)

[3] Lili Wang: Plating & Finishing vol. 20(1998), p.38.

[4] Changsong Dai: Weapons & Engineering vol. 20(1997), p.35.

[5] Hongfei Guo: Plating & Environmental protection vol. 24 (2004), p.1.

[6] Hongxiang Zhang: Plating Technology (Science and technology press in Tianjin, Tianjin 2002).

[7] Jiayou Xu: Surface Technology Vol. 36 (2007), p.65.