The Influence of Hot Rolling Technological Parameters on Microstructure of Low Temperature Grain-Oriented Silicon Steel

Abstract:

The process of hot rolling Fe-3.15% Si steel is simulated by Gleeble-3500 thermal mechanical simulator, the influence of finishing temperature, coiling temperature and cooling rates after rolling on microstructure of Fe-3.15% Si steel are mainly researched, and the influence of hot rolled microstructure on Goss texture, secondary recrystallization and magnetic property are analysed. The results show that the nonuniform microstructures of hot rolled strip play an important role in developing the perfect secondary recrystallization. Fe-3.15% Si steel is rough rolled at 1110°C, finished rolled at 880°C, subsequently cooled to 550°C for coiling at rate of 10°C/s, then air cooled to room temperature. The above mentioned process could produce hot-rolled microstructure which are benefit to formation of Goss texture and the development of perfect secondary recrystallization.

• Periodical: Advanced Materials Research (Volumes 396-398)
• Pages: 1841-1845
• DOI: https://doi.org/10.4028/www.scientific.net/AMR.396-398.1841
• Online since: November 2011
• Authors: Yun Li Feng, Xue Jing Qi, Meng Song
• Keywords: Rolling , Continuous Casting, Microstructure, Si Steel, Thin Slab

References

[1] Zhongzhi He: Metallic Functional Materials Vol. 4 (1997), pp.243-245 (in Chinese)

[2] Tomoji K: Method for producing grain oriented silicon steel sheet having excellent magnetic property (2002)

[3] Hans P: Process for the production of grain-oriented electric quality sheet with low remagnetization loss and high polarization (2003)

[4] Kubota T, Fujikura M and Ushigami Y: Journal of Magnetism and Magnetic Materials (2000)

[5] Xiaoyan Wang, Xuehua Liu and Jing Yao: Iron and Steel Research Vol. 34 (2006), pp.58-62 (in Chinese)

[6] Ruoping Wang, Shide Li and Zemin Fang: Heat Treatment of Metal Vol. 34 (2009), p.1011 (in Chinese)

[7] Yongmei Yu: Ph.D. Dissertation, Northeastern University, Shenyang, 2008 (in Chinese)

[8] Zhenzhen Zhang, Wei Ren and Jianfeng Fang; Special Steel Vol. 32 (2011), pp.68-70 (in Chinese)

[9] Yongmei Yu, Changsheng Li and Yunbo Xu: Journal of Northeastern University Vol. 29 (2008), pp.530-531 (in Chinese)