The Microstructure Transformation of 10CrMo910 Steel after Running 147000h in High Temperature

Zhi Wu Wang; Tao Song; Wei Mei; Cheng Wan

doi:10.4028/www.scientific.net/AMR.430-432.501

Paper Titles

Study on the Residual Compressive Strength of a Composite Sandwich Panel with Foam Core after Low Velocity Impact
p.484

Study on the Catalytic Activity of Graphene Oxide
p.488

Research on the Straightening Deformation Process of the Residual Stress of the Numerical Simulation for Different Kinds of Heavy Rail
p.492

Synthesis and Characterization of Poly(butylenes succinate) with Control Different End-Group
p.497

The Microstructure Transformation of 10CrMo910 Steel after Running 147000h in High Temperature
p.501

A Comparative Study on Wood Properties of Teaks from Different Geographical Provenances
p.508

Inversion Behavior for Cylindrical Tubes under Axial Compression
p.512

Solidification Simulation of Large Flat Ingot in Different Intensive Cooling Conditions
p.517

Preparation of Cordierite–Mullite Composite Crucibles and Structure Characterization
p.521

HomeAdvanced Materials ResearchAdvanced Materials Research Vols. 430-432The Microstructure Transformation of 10CrMo910...

The Microstructure Transformation of 10CrMo910 Steel after Running 147000h in High Temperature

Abstract:

Two specimens from original 10CrMo910 steel and the steel after running 147000h in high temperature were analyzed in this research by SEM, TEM, XRD and electron probe. The results show that after running 147000h in high temperature the 10CrMo910 steel has changed a lot: 1) The dislocation and subgrain boundary in bainite decreased largely while that in massive ferrite almost disappeared. 2) The strip-shape M3C carbides were nearly dissolved, the granular austenite was gradually transformed into martensite, the fine needle-shape Mo2C carbides coarsened, and granular carbides separated out in massive ferrite. 3) There were large particles of M23C6 carbides in crystal boundary between bainite and ferrite, especially in the boundary of any three phases. And creep voids appeared.

You might also be interested in these eBooks

Frontiers of Advanced Materials and Engineering Technology

View Preview

Info:

Periodical:

Advanced Materials Research (Volumes 430-432)

Pages:

501-507

DOI:

https://doi.org/10.4028/www.scientific.net/AMR.430-432.501

Citation:

Cite this paper

Online since:

January 2012

Authors:

Zhi Wu Wang, Tao Song, Wei Mei, Cheng Wan

Keywords:

10CrMo910 Steel, Main Steam Pipe, Microanalysis, Precipitation

Export:

RIS, BibTeX

Price:

Permissions CCC:

Request Permissions

Permissions PLS:

Request Permissions

Сopyright:

Citation:

References

[1] Zhou C Y, Xue J L, Zhang G D. Creep analysis of the pipe with local thinning defect under pressure and moment at high temperature, 5th Fracture Mechanics Symposium，Changsha, PEOPLES R CHINA，(2007).

Google Scholar

[2] Bendick. W, Gabrel. J, Hahn. B, Vandenberghe. B. New low alloy heat resistant ferritic steels T/P23 and T/P24 for power plant application, INTERNATIONAL JOURNAL OF PRESSURE VESSELS AND PIPING, 84(2007) 13-20.

DOI: 10.1016/j.ijpvp.2006.09.002

Google Scholar

[3] Xuan F Z, Tu S D, Wang Z D, Ma C W. EVALUATION OF THE TIME DEPENDENT FAILURE ASSESSMENT CURVES FOR 10CrMo910 AND 316 SS AT 550℃, Acta Metallurgica Sinica(English Letters), 17(2004) 443-449.

Google Scholar

[4] Bourham, M.A. Bourham, M.A. Eddy, W.H. et al. Experimental high heat load surface damage of graphite and refractory materials, Fusion Engineering. 14th IEEE/NPSS Symposium. San Diego, CA. USA. (1991).

DOI: 10.1109/fusion.1991.218799

Google Scholar

[5] Zhu L H, Ma X M. Microstructural evolution of 2. 25Cr-1. 6W-V-Nb heat resistant steel during creep, JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY, 19(2003) 126-128.

Google Scholar

[6] Bourham, M.A. Bourham, M.A. Eddy, W.H. et al. Experimental high heat load surface damage of graphite and refractory materials, Fusion Engineering. 14th IEEE/NPSS Symposium. San Diego, CA. USA. (1991).

DOI: 10.1109/fusion.1991.218799

Google Scholar

[7] Li J F, Liu G P. Carbides Transformation Low of 10CrMo910 for Main steam pipe. North China electric power technology. 9(1995)10-13. (In Chinese).

Google Scholar