The Durability Failure of Pre-Damaged Concrete Induced by Mechanical Load

Abstract:

Chloride ion penetration and freezing and thawing damage are the two main factors that affect the durability of concrete structures. Through the chloride ion penetration test and freezing and thawing test of concrete specimens after tensile and compressive loading, the influence of load-induced damage on the long-term durability of concrete was studied. The results showed that the apparent chloride diffusion coefficient of concrete increased by 6.4% and 34%, and the surface chloride concentration increased 10% and 40%, respectively, both of which showed the "negative effect" when the uniaxial tensile load level reached the 65% and 75% of the ultimate capacity. However, with the increasing uniaxial compressive load level, the impact on the frost resistance of concrete experienced a transformation from the "positive effect" to the "negative effect".

• Periodical: Advanced Materials Research (Volumes 594-597)
• Pages: 1061-1065
• DOI: https://doi.org/10.4028/www.scientific.net/AMR.594-597.1061
• Online since: November 2012
• Authors: Fang Zhi Zhu, Fu Xiang Jiang, Jun Shang, Zhong Hua Bi
• Keywords: Chloride Ion Penetration, Durability Failure, Freezing and Thawing, Mechanical Load

References

[1] W. SUN, Y.M. Zhang, H.D. Yan, et al. Cem Conc Comp, Vol. 21(1999) , p.439–442

[2] MEHTA P K. [S.l.]: Taylor& Francis Group (1991), p.5–10

[3] G. Lin, Z. Wang, J.Z. Lu, et al. Journal of Hydroelectric Engineering, Vol. 3(2001), pp.31-41

[4] Shah, S. P. and Chandra, S. Critical Stress, Volume Change and Microcracking of Concrete, ACI J. (Sept. 1968) 770-780

[5] F.X. Jiang. Durability Mechanism of Concrete and Service Life Forecast Based on Mechanical Damage [D]. Xi'an, 2011.