Analysis on the Cause for Fracture Lamination of 10CrNiCu Steel

Wei Chen; Cong Mao Zhu; Xiang Yan; Wu Qun Liu; Yong Tao Fu

doi:10.4028/www.scientific.net/AMR.602-604.347

Paper Titles

Effect of Intercritical Quenching Temperature on the Microstructure and Performance of 650 MPa Low-Carbon Structural Steel
p.329

Relationships between Fatigue Mechanical Properties and Roughness of Fatigue Fracture about 16MnR Steel after High Temperature
p.333

Effects of Controlled Rolling and Controlled Cooling on the Mechanical Properties of 550MPa Grade Engineering Mechanism Steel
p.337

Influence of Heat Treatment on Mechanical Properties and Microstructure of Mining Machinery Steel Plate Containing Molybdenum and Niobium
p.342

Analysis on the Cause for Fracture Lamination of 10CrNiCu Steel
p.347

Study on Sulfur Control Technology for Non-Oriented Electrical Steel
p.351

On the Presence of Eta Carbide in the Cryogenically Treated High Speed Steel
p.356

Analysis and Practical Application of Extracting Vanadium from Hot Metal in Steel Ladle
p.360

Methodical Basis of Investigation of Influence of the Iron Ore Materials and Coke Metallurgical Characteristics on the Blast Furnace Smelting Efficiency
p.365

HomeAdvanced Materials ResearchAdvanced Materials Research Vols. 602-604Analysis on the Cause for Fracture Lamination of...

Analysis on the Cause for Fracture Lamination of 10CrNiCu Steel

Abstract:

Based on the phenomenon of fracture lamination of 10CrNiCu steel, micro-analysis and Scanning Electron Microscope are applied, and results show that there is a lot of MnS inclusions near the fractures of 10CrNiCu steel，and the banded Structure caused by continuous cast is serious. The improve means is mentioned.