Effects of Frequency and Sonication Time on Ultrasonic Degradation of Natural Rubber Latex

Abstract:

Ultrasonic degradation of fresh latex was investigated at frequencies of 20 and 25 kHz, at a constant temperature of 25^o C (±1^o C) to avoid temperature-related effects. The time-dependent evolution of the molecular weight of the natural rubber latex was determined using gel permeation chromatography, and its structure by means of the fourier transform infrared (FTIR) technique. A 10 minute period of sonication resulted in reduction in the molecular weight of both the 20 and 25 kHz treated samples, the lowest average molecular weight () being obtained in the case of the 25 kHz sample. The of the 25 kHz sample also decreased with increasing latex concentration. However, after 30 minutes, fluctuations had occurred in both samples with respect to the and and also the molecular weight distributions, an effect possibly explained by the competing processes of chain scission and radically-induced cross-linking of the polymer chains. The FTIR results also suggest that the structure of polyisoprene is unaltered by ultrasonic wave treatment at these frequencies.

• Periodical: Advanced Materials Research (Volume 747)
• Pages: 721-724
• DOI: https://doi.org/10.4028/www.scientific.net/AMR.747.721
• Online since: August 2013
• Authors: S. Utara, U. Moonart
• Keywords: Molecular Weight, Natural Rubber Latex (NRL), Sonication Time, Ultrasonic Degradation

References

[1] M. Yin, P. Cui, Z. Hu, Y. Chen, W. Xiong, Effect of ultrasonic intensity on the degradation of phenol solution, Adv. Mat. Res. 393-396 (2011) 1173-1176.

DOI: 10.4028/www.scientific.net/amr.393-395.1173

[2] J.M.J. Paulusse, R.P. Sijbesma, Ultrasound in polymer chemistry: revival of the establised technique, J. Polym. Sci. Part A: Polym. Chem. 44(2006) 5445-5453.

DOI: 10.1002/pola.21646

[3] M.T. Taghizadeh, T. Asadpour, Effect of molecular weight on the ultrasonic degradation of poly(vinyl-pyrrolidone), Ultrason. Sonochem. 15 (2009) 280-286.

DOI: 10.1016/j.ultsonch.2008.07.010

[4] G.J. Price, P.F. Smith, Ultrasonic degradation of polymer solutions: 1. Polystyrene revisited, Polym. Int. 24(1991) 159-163.

DOI: 10.1002/pi.4990240306

[5] G.J. Price, P.F. Smith, Ultrasonic degradation of polymer solutions: 2. the effect of temperture, ultrasound intensity and disolved gases on polystyrene in toluene, Polymer 34(1993) 4111–4117.

DOI: 10.1016/0032-3861(93)90675-z

[6] G.J. Price, P.F. Smith, Ultrasonic degradation of polymer solutions: 3. effect of changing solvent and solution concentration, Eur. Polym. J. 29(1993) 419–424.

DOI: 10.1016/0014-3057(93)90114-u

[7] Y. Li, J. Li, S. Guo, H. Li, Mechanochemical degradation kinetics of high-density polyethylene melt and its mechanism in the presence of ultrasonic irradiation, Ultrason. Sonochem. 12(2005) 183-189.

DOI: 10.1016/j.ultsonch.2003.10.011

[8] H. Yen, M. H, Yang, The ultrasoic degadation of polyacrylamide solution, Polym. Test. 22(2003) 129-131.

[9] G. Madras, S. Chattopadhyay, Effect of solvent on the ultrasoinc degradation of poly(vinyl acetate), Polym. Degrad. Stabi. 71(2001) 273-278.

DOI: 10.1016/s0141-3910(00)00174-9

[10] Z. Xiaodong, L. Qunfang, D. Gance, J. Faxiang, Ultrasonic degradation of polysilane polymers, Polym. Degrad. Stabi. 60(1998) 409-413.

DOI: 10.1016/s0141-3910(97)00101-8

[11] K. Hunseung, K.Y. Min, K.H. Han, Identification of Natural Rubber and Characterization of Rubber Biosynthetic Activity in Fig Tree, Plant Physiol. 123 (2000) 1133-1142.

DOI: 10.1104/pp.123.3.1133

[12] S. Utara, P. Boochatum, Effect of molecular weight of natural rubber on the compatibility and crystallization behavior of LLDPE/NR blends, Polym. Plast. Technol. Eng. 50 (2011) 1019-1026.

DOI: 10.1080/03602559.2011.557819

[13] A. Gronoroos, P. Pentti, K. Hanna, Ultrasonic degradation of aqueous carboxymethylcellulose: effect of viscosity, molecular mass, and concentration, Ultrason. Sonochem. 15 (2008) 644-648.

DOI: 10.1016/j.ultsonch.2007.09.005