The Preparation of Aniline Formaldehyde Condensate-Mesoporous Materials Compound and the Application in Adsorption of Zn(II) and Pb(II) in Aqueous Solution

Yan Liu; Ze Yang Zhu; Xiang Guo Meng; Hai Xu Yin; Min Jia Meng; Juan Han; Yun Wang; Rui Chen

doi:10.4028/www.scientific.net/AMR.781-784.2229

Paper Titles

Design, Synthesis and Biological Evaluation of of Novel Anticancer Agent tert-butyl 1-phenyl-3,4-dihydro-1H-pyrido[3,4-b]indole-2(9H)-carboxylate
p.2211

Impact of Soil Surface Charge Properties on Migration Behavior of Radioactive Uranium, Strontium and Cesium
p.2215

Determination of Pesticide in Soil-Water System by Solid Phase Extraction and Gas Chromatography
p.2221

Preparation of Sodium Ferrate by Microwave Method
p.2225

The Preparation of Aniline Formaldehyde Condensate-Mesoporous Materials Compound and the Application in Adsorption of Zn(II) and Pb(II) in Aqueous Solution
p.2229

Removal of Cr(VI) from Water Using Attapulgite/Chitosan Composites
p.2233

Photocatalytic Properties of Nitrogen-Sulfur Co-Doped TiO₂ Films Coated on Glass Fiber
p.2237

Treatment of Oily Wastewater by Photocatalytic Degradation Using Nano Fe-TiO₂
p.2241

UV Photodegradation and Anaerobic Digestion of MB Dye
p.2245

HomeAdvanced Materials ResearchAdvanced Materials Research Vols. 781-784The Preparation of Aniline Formaldehyde...

The Preparation of Aniline Formaldehyde Condensate-Mesoporous Materials Compound and the Application in Adsorption of Zn(II) and Pb(II) in Aqueous Solution

Abstract:

The amine aldehydes resin-mesoporous materials complex AFC-SBA-15 was synthesized using ordered mesoporous materials SBA-15 as the carrier. The obtained compound was characterized by FT-IR,N₂ adsorption-desorption and scanning electron microscopy. The compound retained ordered mesoporous structure and the resin polymer coated inside channels and outside surface hole wall. The adsorption behavior was carried out with the presence of EDTA in binary components of Pb (II) and Zn (II). The result showed that with the presence of EDTA, tunable selectivity could be realized.