N,N-Diethylammonium O,O’-Di(3-methylphenyl)dithiophosphate as Corrosion Inhibitor for Q235 Steel in HCL Solution

Sha Sha Zhu; Qin Huan Yang; Bin Xie; Yu Long Li; Xiao Lin; Jian Shen Feng; Li Ke Zou

doi:10.4028/www.scientific.net/AMR.781-784.291

Paper Titles

Synthesis of Butanone 1,2 - Propanediol Ketal by Sulfamic Acid as Catalyzed
p.276

Synthesis of LC Intermediate Containing Trimethyl Silyl Acetylene Group
p.280

A Novel Process for Synthesis of Cyclohexyl Ferulate
p.283

A New Method for the Biomimetic Synthesis of 2-Hydroxy-3-Amino-1,4-Naphthoquinone
p.287

N,N-Diethylammonium O,O’-Di(3-methylphenyl)dithiophosphate as Corrosion Inhibitor for Q235 Steel in HCL Solution
p.291

Adsorption Behavior and Corrosion Inhibition of S-benzyl-O,O'-dibenzyldithiophosphate for Carbon Steel in Hydrochloric Acid Solution
p.295

Corrosion Inhibition of N,N- diethylammonium O,O′- di (p-chlorophenyl) dithiophosphate for Carbon Steel in HCL Solution
p.299

Synthesis and Hydrodesulfurization Performance of NiMo Sulfide Catalysts Supported on γ-Al₂O₃
p.304

Research on the Catalytic Activity of Mn_yCe_zO_x/TiO₂ for Ethyl Acetate Oxidation
p.308

HomeAdvanced Materials ResearchAdvanced Materials Research Vols. 781-784N,N-Diethylammonium...

N,N-Diethylammonium O,O’-Di(3-methylphenyl)dithiophosphate as Corrosion Inhibitor for Q235 Steel in HCL Solution

Abstract:

The corrosion inhibition of N,N-diethylammonium O,O-di (3-methylphenyl) dithio-phosphate (NDOMD) for Q235 steel in HCl solution was studied by electrochemical measurements and weight loss measurements. And the effects of temperature, HCl concentration and immersion time were also studied. Polarization curves indicate the NDOMD is a mixed-type inhibitor which anodic plays a leading role. The studies of weight loss measurement show that the inhibition efficiency was up to 94.46% at the NDOMD concentration of 100 mg·L^-1 in 1.0 mol.L^-1 HCl solution at 30°C. The adsorption of NDOMD on Q235 steel surface obeys the Langmuir isotherm.