Synthesis and Properties Study of Poly-di(bis-dimethoxy-ethyl) Amine Phosphazene

Lin Tao Zhou; Dong Mei Luo; Guo Bin Li; Yi Su

doi:10.4028/www.scientific.net/AMR.781-784.515

Paper Titles

Synthesis, Characterization of 2',7'-dibromo-2,3,6,7-tetraethoxy-9,9'-spirobifluorene
p.499

Synthesis of a Biodegradable Material Poly(lactic acid-co-melamine) via Direct Melt Polycondensation
p.503

Study on Luminescence Properties of Bipolar Copolymers Containing Quinoline Aluminum and Carbazole Groups
p.507

Study on the Role of Surfactants to Aqueous Two-Phase Synthesizing CPAM
p.511

Synthesis and Properties Study of Poly-di(bis-dimethoxy-ethyl) Amine Phosphazene
p.515

R-ATRP of Acrylamide under the Action of Iron Complex System in Inverse Emulsion
p.521

Preparation and Characterization of Cationic Cassia Tora Gum
p.526

Supramolecular Structure in the Cocrystal of 3, 5-Bispyridyl-1-H-1, 2, 4-Triazole and 4,4-Oxybis(Benzoic Acid)
p.531

Synthesis and Properties of Thermo- and pH-Sensitive Poly[(Sodium Humate)-(N-Isopropylacrylamide)-(Acrylic Acid)] Intelligent Hydrogel
p.536

HomeAdvanced Materials ResearchAdvanced Materials Research Vols. 781-784Synthesis and Properties Study of...

Synthesis and Properties Study of Poly-di(bis-dimethoxy-ethyl) Amine Phosphazene

Abstract:

Poly-di (bis-dimethoxy-ethyl) amine phosphazene was synthesized by nucleophilic substitution reaction with bis (dimethoxy ethyl) amine and conductive polymer materials were manufactured by compositing of the lithium salt and polyphosphazene. The results show that: T_d10 =503K, the maximum decomposition rate was at 653K. When the mol Li⁺/ repeat unit was 1.5, the conductivity of polyphosphazene composite conductive material comes up to 4.21×10^-8S/cm.