Chloride Diffusion in Limestone Cement Concrete Exposed to Combined Chloride and Sulfate Solutions at Low Temperature

Abstract:

The chloride diffusion in limestone cement concrete exposed to combined chloride and sulfate solutions at low temperature was studied. For this purpose, a normal Portland cement and two Portland limestone cements (15% and 35% w/w limestone content) were used for concrete preparation. The specimens were immersed in two combined chloride-sulfate solutions of different sulfate content, and stored at 5°C. The total and free chloride contents, as well as the chloride diffusion coefficients were determined for each concrete composition. The results show that the total chloride content and free to total chloride ratio are increased with time. The sulfate content of the corrosive solutions has not a clear effect on total chloride content and chloride diffusion coefficient. It seems that the lower sulfate content results, in general, in higher free to total chloride ratio values. The use of limestone in cement results in higher chloride concentrations in concrete and free to total chloride ratio values. In general, these phenomena are intensified for higher limestone content.

• Periodical: Advanced Materials Research (Volume 897)
• Pages: 171-175
• DOI: https://doi.org/10.4028/www.scientific.net/AMR.897.171
• Online since: February 2014
• Authors: Konstantinos Sotiriadis, Sotirios Tsivilis, Vít Petranek
• Keywords: Chloride Diffusion, Limestone Cement Concrete, Low Temperature, Sulfate

References

[1] European Committee for Standardization, EN 197–1. EN/TC 51/WG 6, (2011).

[2] S. Tsivilis, E. Chaniotakis, E. Badogiannis, G. Pahoulas and A. Ilias: Cem. Concr. Compos. Vol. 21 (1999), p.107.

[3] E.F. Irassar: Cem. Concr. Res. Vol. 39 (2009), p.241.

[4] J. Bensted: Cem. Concr. Compos. Vol. 21 (1999), p.117.

[5] A. Skaropoulou, S. Tsivilis, G. Kakali, J.H. Sharp and R.N. Swamy: Cem. Concr. Compos. Vol. 31 (2009), p.628.

[6] H. -J. Chen, Sh. -S. Huang, Ch. -W. Tang, M.A. Malek and L. -W. Ean: Constr. Build. Mater. Vol. 35 (2012), p.1063.

[7] U. Angst, B. Elsener, C.K. Larsen and Ø. Vennesland: Cem. Concr. Res. Vol. 39 (2009), p.1122.

[8] K.Y. Ann and H. -W. Song: Corros. Sci. Vol. 49 (2007), p.4113.

[9] T. Cheewaket, C . Jaturapitakkul and W. Chalee: Constr. Build. Mater. Vol. 24 (2010), p.1352.