Effect of New Corrosion Inhibitor on Electrochemical Behavior of Prestressed Steel Wire in Simulated Concrete Pore Solution

Abstract:

The polarization curve and AC impedance are used to study the impacts of new corrosion inhibitor on the prestressed steel wire electrochemistry action in the simulated concrete pore solution. The result shows that, the ammonium molybdate, DETA, propylene thiourea, 1,4-butynediol and other compound corrosion inhibitors are positive inhibitory corrosion inhibitors, with the components of passivator and healant of protective oxide film, which can contribute to the formation of a passive film of oxide on the rebar surface, repair the defects of rebar surface, coat the entire rebar with a passive film of oxide with good compactness and stability, prevent the chloride ion from penetration, reduce the free rate of iron ions, and thus achieve the anti-corrosion purpose.

• Periodical: Advanced Materials Research (Volumes 941-944)
• Pages: 1390-1393
• DOI: https://doi.org/10.4028/www.scientific.net/AMR.941-944.1390
• Online since: June 2014
• Authors: Qi Lei Sun*, Ze Rui Liu, Yun Zhu Guo, Feng Liu
• Keywords: Corrosion Inhibitor, Electrochemical Impedance Spectroscopes, Polarization Curve, Prestressed Steel Wire, Simulated Concrete Pore Solution

References

[1] Schupack M. A survey of the durability performance of post-tensioning tendons[J]. ACI Journal, 1978, 75(10): 501-510.

[2] Schupack M, Suarez M G. Some recent corrosion embrittlement failures of prestressing system s in the United States[J] . PCI Journal, 1982, 27(2): 38-55.

DOI: 10.15554/pcij.03011982.38.55

[3] Nurnberger U. Corrosion protection o f prestressing steels[R]. London: FIP State-of-the-Art Report, (1986).

[4] Vehova r L, Kuhar V, Vehovar A. Hydrogen-assisted stress-corrosion of prestressing wires in a motoway viaduct [J]. Engineering Failure Analysis, 1998, 5(1): 21-27.

DOI: 10.1016/s1350-6307(97)00034-4

[5] Valiente A. Stress corrosion failure o f large diameter pressure pipe lines of prestressed concrete[ J]. Engineering Failure Analysis, 2001, 8(3): 245-261.

DOI: 10.1016/s1350-6307(00)00010-8

[6] Salas R M, Schokker A J, West J S, et al. Corrosion risk of bonded, post-tensioned concrete element [J] . PCI Journal, 2008, 53(1): 89-107.

DOI: 10.15554/pcij.01012008.89.108

[7] Liu X M, Song G L, Lin H C, et al. A study survey of destruction caused by reinforcing steel in concrete [J]. Mater. Prot. 1996, 29(6)：16-18.

[8] Wang Ying, He Ping, Shi Yuanxiang, etc. The Action Mechanism of Corrosion Inhibitor to the Rebar in the Simulated Concrete Pore Solution and Motar [J], Journal of Nanjing University of Chemical Technology, 1998 , 20 (2) : 53 - 57.