Paper Titles

Analytical Determination of Mixed-Mode Energy Release Rates for Delamination Using a Crack Tip Element
p.161

Computational Structural Analysis and Testing: An Approach to Understand Delamination Growth
p.181

Using Stress Smoothing for Interlaminar Stress Distribution in Finite Element Analysis of Composite Laminates
p.203

Damage Mechanisms and Fracture Modes in Nicalon / CAS-II Laminates
p.227

Recent Research on Damage Development in SiC/Ti Continuous Fiber Metal Matrix Composites
p.257

Failure Prediction of Composite Laminates under Torsion
p.285

Stress Determination and Core Failure Analysis in Sandwich Rampdown Structures under Bending Loads
p.307

Interlaminar Fracture Characterization
p.329

Fracture of Double Beam Specimens Containing 90-Degree Plies
p.347

HomeKey Engineering MaterialsKey Engineering Materials Vols. 120-121Recent Research on Damage Development in SiC/Ti...

Recent Research on Damage Development in SiC/Ti Continuous Fiber Metal Matrix Composites

Article Preview

Abstract:

You might also be interested in these eBooks

Fracture of Composites

Info:

Periodical:

Key Engineering Materials (Volumes 120-121)

Pages:

257-284

DOI:

https://doi.org/10.4028/www.scientific.net/KEM.120-121.257

Citation:

Cite this paper

Online since:

May 1996

Authors:

David H. Allen, M.R. Eggleston, L.D. Hurtado

Keywords:

Damage, Environmental Degradation, Fracture, Life Prediction, Metal Matrix Composite (MMC), Viscoplasticity

Export:

RIS, BibTeX

Price:

Permissions CCC:

Request Permissions

Permissions PLS:

Request Permissions

Сopyright:

© 1996 Trans Tech Publications Ltd. All Rights Reserved

Share:

Citation: