Effect of Vickers Indented Load and Microstructure on Hardness, Bending Strength and Fracture Toughness in Sintered Silicon Carbide Ceramics
p.155

Effect of Stress Corrosion Cracking on Fracture Strength of Si₃N₄
p.161

Particle Impact Damage in Silicon Carbide
p.167

Particle Impact Damage on Ceramics
p.173

Mechanics Approach to Fracture Strength of Ceramics/Metal Joints
p.179

The Evaluation of the Strength of Adhesive Joints by Application of Fracture Mechanics
p.185

HomeKey Engineering MaterialsKey Engineering Materials Vols. 51-52Effect of Stress Corrosion Cracking on Fracture...

Effect of Stress Corrosion Cracking on Fracture Strength of Si₃N₄

Article Preview

Abstract:

You might also be interested in these eBooks

Fracture and Strength '90

Info:

Periodical:

Key Engineering Materials (Volumes 51-52)

Pages:

161-166

DOI:

https://doi.org/10.4028/www.scientific.net/KEM.51-52.161

Citation:

Cite this paper

Online since:

January 1991

Authors:

H. Kobayashi, Yoshikazu Arai, S.Ch. Hwang, S. Kani

Keywords:

Ceramic, Fracture Strength, Fracture Toughness, Indentation Strength Method, Stress Corrosion Cracking (SCC)

Export:

RIS, BibTeX

Price:

Permissions CCC:

Request Permissions

Permissions PLS:

Request Permissions

Сopyright:

© 1991 Trans Tech Publications Ltd. All Rights Reserved

Share:

Citation: