Effect of Post-Weld Heat Treatment on Hardness in Superduplex Stainless Steel ASTM A890/A890M - Grade 6A

Clélia Ribeiro de Oliveira; Eloá Lopes Maia; Solange T. da Fonseca; Marcelo Martins; Julián Arnaldo Ávila Díaz; Paulo Roberto Mei

doi:10.4028/www.scientific.net/MSF.1012.296

Paper Titles

The Use of Thermogravimetric Analysis to Characterize the Metallic Slag Aggregates in Structural Concrete
p.272

Selective Laser Sintering of Biomaterials and Composites State of the Art and Perspectives
p.278

Citric Acid Effect in High early Type Portland Cement Pastes and Mortars
p.284

Equal Channel Angular Pressing Consolidation and Heat Treatment of Blended Elemental Powders of Fe-Mn-Al
p.291

Effect of Post-Weld Heat Treatment on Hardness in Superduplex Stainless Steel ASTM A890/A890M - Grade 6A
p.296

Microstructural Characterization and Mathematical Modeling for Determination of Volume Fraction of Eutectoid Mixture of the Cu-8.5wt% Sn Alloy Obtained by Unidirectional Upward Solidification
p.302

Influence of the Thermal Parameters on the Microstructure, Corrosion Resistance and Hardness on the Unidirectional Solidification of Al-10wt% Si-5wt% Cu Alloy
p.308

PrFeB Based Alloys Obtained by Melt Spinning for the Production of Permanent Magnets
p.314

Mechanical Resistance of High-Speed Steels Cr-W-Mo-V, Si-Mn-Cr-Mo-V-Co, Si-Mn-Cr-Mo-V and Si-Mn-Cr-Mo-V-Co Heat Treated
p.319

HomeMaterials Science ForumMaterials Science Forum Vol. 1012Effect of Post-Weld Heat Treatment on Hardness in...

Effect of Post-Weld Heat Treatment on Hardness in Superduplex Stainless Steel ASTM A890/A890M - Grade 6A

Abstract:

Superduplex stainless steel alloy exhibit high mechanical and corrosion resistance, which main industrial application is in the petrochemical industry. The manufacture and maintenance of such equipment usually involve welding processes, followed by post-welded heat treatment and it often becomes impossible to apply heat treatments. Thereby, the purpose of this work is to verify the effect of a post-welded heat treatment on shielded metal arc welding in steel grade ASTM A890/A890M - grade 6A. The microstructure in the as-welded condition consisted of austenite, secondary austenite, and ferrite phases and, the post-welded heat treatment condition exhibited only austenite and ferrite. The hardness in the melt zone reached values of 300 HV after welding and, the value was reduced to 260 HV in the post-welded heat treatment condition.

You might also be interested in these eBooks

23rd Brazilian Conference on Materials Science and Engineering

View Preview

Info:

Periodical:

Materials Science Forum (Volume 1012)

Pages:

296-301

DOI:

https://doi.org/10.4028/www.scientific.net/MSF.1012.296

Citation:

Cite this paper

Online since:

October 2020

Authors:

Clélia Ribeiro de Oliveira*, Eloá Lopes Maia, Solange T. da Fonseca, Marcelo Martins, Julián Arnaldo Ávila Díaz, Paulo Roberto Mei

Keywords:

ASTM A890/A890M Standard, Post-Welded Heat Treatment, Superduplex Stainless Steels, Vickers Hardness

Export:

RIS, BibTeX

Price:

Permissions CCC:

Request Permissions

Permissions PLS:

Request Permissions

Сopyright:

Citation:

* - Corresponding Author

References

[1] ASTM A890/A890M - 13, Standard Specification for Castings, Iron-Chromium-Nickel-Molybdenum Corrosion- Resistant, Duplex (Austenitic/Ferritic) for General Application1, ASTM Int., 01.02 (2014) 1–5.

DOI: 10.1520/a0890_a0890m-99r07

Google Scholar

[2] S. Atamert, J.E. King: Mater. Sci. Technol. Vol. 8 (1992), p.896.

Google Scholar

[3] J. Charles: Rev. Métallurgie Vol. 105 (2008), p.5.

Google Scholar

[4] J.O. Nilsson: Mater. Sci. Technol. Vol. 8 (1992), p.685.

Google Scholar

[5] A.I. Mourad, A. Khourshid, T. Sharef: Mater. Sci. Eng. A Vol. 549 (2012), p.105.

Google Scholar

[6] J.D. Kordatos, G. Fourlaris, G. Papadimitriou: Mater. Sci. Forum Vols. 318–320 (1999), p.615.

Google Scholar

[7] K.R. Gadelrab, G. Li, M. Chiesa: J. Mater. Res. (2012).

Google Scholar

[8] A. Vinoth Jebaraj, L. Ajaykumar, C.R. Deepak, K.V.V. Aditya: J. Adv. Res. Vol. 8 (2017), p.183.

Google Scholar

[9] P. Dong, S. Song, J. Zhang: Int. J. Press. Vessel. Pip. Vol. 122 (2014), p.6.

Google Scholar

[10] Z. Zhang, H. Zhang, J. Hu, X. Qi, Y. Bian, A. Shen, P. Xu, Y. Zhao: Constr. Build. Mater. Vol. 168 (2018), p.338.

Google Scholar

[11] ASTM E384 - 11, Standard Test Method for Knoop and Vickers Hardness of Materials, ASTM Int. (2012) 1–43.

Google Scholar