Second Phase Dissolution Influenced by Simultaneously Enhanced Mg, Cu Contents during Homogenization of As-cast Al-Zn-Mg-Cu Alloys

Article Preview

Abstract:

The dissolution of second phase with relatively high melting point in as-cast Al-Zn-Mg-Cu alloys was closely related to Mg and Cu contents. In present work, second phases in three Al-Zn-Mg-Cu alloys with simultaneously enhanced Mg and Cu contents (named by LMC alloy, MMC alloy and HMC alloy as Mg and Cu contents progressively enhanced) were analyzed and the correlated dissolution during homogenization was investigated. The results showed that both Mg(Zn,Cu,Al)2 phase and Cu-rich phase existed in as-cast alloys while HMC alloy possessed more eutectic phases. As homogenized by 470°C/24h, Mg(Zn,Cu,Al)2 phase had dissolved completely, LMC alloy contained little Al2CuMg phase and the amount of it for the three alloys was arranged as LMC alloy < MMC alloy < HMC alloy. As furtherly homogenized by a second stage at 480°C for 12h, no endothermic peak for Al2CuMg phase was observed for LMC alloy and only Fe-rich phase existed. Meanwhile, Al2CuMg phase still remained in MMC and HMC alloy. As the homogenization time prolonging to 36h, Al2CuMg phase in MMC alloy dissolved completely while that still existed in HMC alloy. Adding a third stage at 490°C for HMC alloy, no Al2CuMg phase could be observed for 24h. This gave rise to a method by incrementally grading homogenization temperature combined with prolonging soaking time to fulfill the dissolution of second phase for Al-Zn-Mg-Cu alloys with enhanced Mg and Cu contents

You might also be interested in these eBooks

Info:

Periodical:

Materials Science Forum (Volume 1071)

Pages:

11-19

Citation:

Online since:

October 2022

Export:

Price:

Permissions CCC:

Permissions PLS:

Сopyright:

© 2022 Trans Tech Publications Ltd. All Rights Reserved

Share:

Citation:

* - Corresponding Author

[1] P. Jarry, M. Rappaz. Recent advances in the metallurgy of aluminium alloys. Part I: Solidification and casting, CR Phys. 2018, 19(8): 672-687.

DOI: 10.1016/j.crhy.2018.09.003

Google Scholar

[2] T. Dursun, C. Soutis. Recent developments in advanced aircraft aluminium alloys, Mater. Des. 2014, 56(4): 862-871.

DOI: 10.1016/j.matdes.2013.12.002

Google Scholar

[3] B. Zhou, B. Liu, S. Zhang. The Advancement of 7XXX Series Aluminum Alloys for Aircraft Structures: A Review, Metals, 2021, 11(5): 718.

DOI: 10.3390/met11050718

Google Scholar

[4] A. Azarniya, A.K. Taheri, K.K. Taheri. Recent advances in ageing of 7xxx series aluminum alloys: A physical metallurgy perspective, J. Alloys Compd. 2019, 781: 945-983.

DOI: 10.1016/j.jallcom.2018.11.286

Google Scholar

[5] P.A. Rometsch, Y. Zhang, S. Knight. Heat treatment of 7xxx series aluminium alloys—Some recent developments, Trans. Nonferrous Metals Soc. 2014, 24(7): 2003-2017.

DOI: 10.1016/s1003-6326(14)63306-9

Google Scholar

[6] H.C. Fang, H. Chao, K.H. Chen. Effect of recrystallization on intergranular fracture and corrosion of Al–Zn–Mg–Cu–Zr alloy, J. Alloys Compd. 2015, 622: 166-173.

DOI: 10.1016/j.jallcom.2014.10.044

Google Scholar

[7] A.R. Eivani, H. Ahmed, J. Zhou, et al. An experimental and theoretical investigation of the formation of Zr-containing dispersoids in Al–4.5Zn–1Mg aluminum alloy, Mater. Sci. Eng. A. 2010, 527(9): 2418-2430.

DOI: 10.1016/j.msea.2010.01.012

Google Scholar

[8] Z. Shan, S. Liu, L. Ye, et al. Effect of three-stage homogenization on recrystallization and fatigue crack growth of 7020 aluminum alloy, J. Mater. Res. Technol. 2020, 9(6): 13216-13229.

DOI: 10.1016/j.jmrt.2020.09.066

Google Scholar

[9] H. Wu, S.P. Wen, H. Huang, et al. Effects of homogenization on precipitation of Al3(Er,Zr) particles and recrystallization behavior in a new type Al-Zn-Mg-Er-Zr alloy, Mater. Sci. Eng. A. 2017, 689: 313-322.

DOI: 10.1016/j.msea.2017.02.071

Google Scholar

[10] H. Lin, L. Ye, L. Sun, et al. Effect of three-step homogenization on microstructure and properties of 7N01 aluminum alloys, T. Nonferrous Metals Soc. 2018, 28(5): 829-838.

DOI: 10.1016/s1003-6326(18)64716-8

Google Scholar

[11] L. Wu, W. Wang, Y. Hsu, et al. Effects of homogenization treatment on recrystallization behavior and dispersoid distribution in an Al–Zn–Mg–Sc–Zr alloy, J. Alloys Compd. 2008, 456(1-2): 163-169.

DOI: 10.1016/j.jallcom.2007.02.054

Google Scholar

[12] H. Wu, S. Wen, J. Lu, et al. Microstructural evolution of new type Al–Zn–Mg–Cu alloy with Er and Zr additions during homogenization, T. Nonferrous Metals Soc. 2017, 27(7): 1476-1482.

DOI: 10.1016/s1003-6326(17)60168-7

Google Scholar

[13] E. Acer, E. çadırlı, H. Erol, et al. Effect of heat treatment on the microstructures and mechanical properties of Al-5.5Zn-2.5Mg alloy, Mater. Sci. Eng. A. 2016, 662: 144-156.

DOI: 10.1016/j.msea.2016.03.073

Google Scholar

[14] Y. Liu, D. Jiang, W. Xie, et al. Solidification phases and their evolution during homogenization of a DC cast Al–8.35Zn–2.5Mg–2.25Cu alloy, Mater. Charact. 2014, 93: 173-183.

DOI: 10.1016/j.matchar.2014.04.004

Google Scholar

[15] J. Liu, Y. Zhang, X. Li, et al. Phases and microstructures of high Zn-containing Al–Zn–Mg–Cu alloys, Rare Metals. 2016, 35(5): 380-384.

DOI: 10.1007/s12598-014-0222-6

Google Scholar

[16] D. Xu, Z. Li, G. Wang, et al. Phase transformation and microstructure evolution of an ultra-high strength Al-Zn-Mg-Cu alloy during homogenization, Mater. Charact. 2017, 131: 285-297.

DOI: 10.1016/j.matchar.2017.07.011

Google Scholar