Comparing Different Methods to Determine the Intergranular Oxidation Damage on a Nickel Based Superalloy

Abstract:

Article Preview

Info:

Periodical:

Materials Science Forum (Volumes 461-464)

Edited by:

Pierre Steinmetz, Ian G. Wright, Gerry Meier, Alain Galerie, Bernard Pieraggi and Renaud Podor

Pages:

537-544

Citation:

V. Garat et al., "Comparing Different Methods to Determine the Intergranular Oxidation Damage on a Nickel Based Superalloy", Materials Science Forum, Vols. 461-464, pp. 537-544, 2004

Online since:

August 2004

Export:

Price:

$38.00

[1] C.S. Giggins and F.S. Pettit: Transactions of the Metallurgical Society of AIME Vol. 245 (1969), p.2495.

[2] H.E. Evans: Int. Mater. Rev. Vol. 40.

[1] (1995), p.1.

[3] G.A. Greene and C.C. Finfrock: Oxid. Met. Vol. 55 [5-6] (2001), p.505.

[4] V. Suresh Babu, A.S. Pavlovic and M.S. Seehra: Superalloys 718, 625, 706 and Various Derivative, (1997), p.689.

[5] D. M. England and A.V. Virka: J. Electrochemi. Soc. Vol. 146.

[9] (1999), p.3196.

[6] R. Molins, PhD Thesis, ENSM Paris, France, (1995).

[7] C.F. Miller, G.W. Simmons and R.P. Wei: Scripta Mater. Vol. 44 (2001), p.2405.

[8] J. Panter, M. Foucault, P. Combrade, B. Viguier and E. Andrieu, Corrosion NACE, April 2002, paper #02519.

[9] O. Brucelle, PhD Thesis, INP Toulouse, France, 2001. 10 µm External oxide Non bearing zone Prior to deformation Intergranular oxide penetration Material After plastic deformation (ε) 10 µm 10(1+ε)µm Interface Detectable IOP opening.

Fetching data from Crossref.
This may take some time to load.