Magnetic Structure and Magnetization Reversal in Nanocomposite Pr2Fe14B/α-Fe Ribbons

Xiaoqian Bao; Mao Cai Zhang; Yi Qiao; Shouzeng Zhou

doi:10.4028/www.scientific.net/MSF.475-479.2127

Paper Titles

On Control of Six Freedom Magnetostrictive Smart Structure
p.2111

Research on the Model of the Magnetostrictive Actuator
p.2115

Damage Localization on Two-Dimensional Structure Based on Wavelet Transform and Active Lamb Wave-Based Method
p.2119

Defects Distribution of Pr₂Fe₁₄B Hard Magnetic Magnet from Amorphous to Nanostructures Characterized by Positron Annihilation Spectroscopy
p.2123

Magnetic Structure and Magnetization Reversal in Nanocomposite Pr₂Fe₁₄B/α-Fe Ribbons
p.2127

Magnetic Properties of Fe-Pt Nanoparticle Protected by PVP Polymer
p.2131

Magnetic Stability of Fe-Cr-Co Permanent Magnet Materials at High Temperature
p.2135

Mössbauer Spectrometry Study of Spinodal Decomposition in Fe-25Cr-12Co-1Si Alloy during Step Ageing
p.2139

Study on Manufacture of 2:17 Sm-Co Magnets by Powder Injection Molding
p.2143

HomeMaterials Science ForumMaterials Science Forum Vols. 475-479Magnetic Structure and Magnetization Reversal in...

Magnetic Structure and Magnetization Reversal in Nanocomposite Pr₂Fe₁₄B/α-Fe Ribbons

Abstract:

Nanocomposite Pr7.5Dy1Fe71Co15Nb1B4.5 ribbons were prepared by melt-spinning and subsequent annealing. Interaction domains were imaged using magnetic force microscopy (MFM) because of strong exchange coupling between hard and soft magnetic grains. Coercivity was determined by exchange coupling pinning field. But the magnetization reversal of nanocomposite magnets were different from that of traditional single phase permanent magnets.

You might also be interested in these eBooks

View Preview

Info:

Periodical:

Materials Science Forum (Volumes 475-479)

Pages:

2127-2130

DOI:

https://doi.org/10.4028/www.scientific.net/MSF.475-479.2127

Citation:

Cite this paper

Online since:

January 2005

Authors:

Xiaoqian Bao, Mao Cai Zhang, Yi Qiao, Shouzeng Zhou

Keywords:

Interaction Domain, Magnetization Reversal, Nanocomposite Permanent Magnets

Export:

RIS, BibTeX

Price:

Permissions CCC:

Request Permissions

Permissions PLS:

Request Permissions

Сopyright:

Citation:

References

[1] E.F. Kneller and R. Hawig: IEEE Trans. Magn. Vol. 27 (1991), p.3588.

Google Scholar

[2] R. Skomski and J.M.D. Coey: Phys. Rev. B Vol. 48 (1993), p.15812.

Google Scholar

[3] Z.C. Wang, S.Z. Zhou, M.C. Zhang: J. Appl. Phys. Vol. 88 (2000), p.591.

Google Scholar

[4] X.Y. Zhang, Y. Guan, L. Yang: Appl. Phys. Lett Vol. 79 (2001), p.2426.

Google Scholar

[5] E.F. Kneller, R. Hawig: IEEE Trans. Magn. Vol. 27 (1991), p.3588.

Google Scholar

[6] G.C. Hadjipanayis: J. Magn. Magn. Mater. Vol. 200 (1999), p.373.

Google Scholar

[7] H.W. Zhang, Z.G. Sun, S.Y. Zhang: Phys. Rev. B Vol. 60 (1999), p.64.

Google Scholar

[8] G.E. Carr, H.A. Davies, and R.A. Buckley: Mater. Sci. Eng. Vol. 99 (1988), p.142.

Google Scholar

[9] G.C. Hadjipanayis, W. Gong: J. Magn. Magn. Mater. Vol. 66 (1987), p.390.

Google Scholar

[10] H.A. Davies: J. Magn. Magn. Mater. Vol. 157-158 (1996), p.11.

Google Scholar

[11] E.P. Wohlfarth. J. Appl. Phys. Vol. 29 (1958), p.595 Fig. 5 Typical magnetization curves of melt-spun and heat-treated samples 0 200 400 600 800 1000 1200 1400 1600.

[1] 0.

[1] 2.

[1] 4.

[1] 6 as-spun 5min 15min 120min J (T) H (kA. m -1 ) Fig. 6 Typical hysteresis loops of melt-spun and heat-treated samples -2000 -1500 -1000 -500 0 500 1000 1500 2000 -1. 5 -1. 0 -0. 5.

Google Scholar

[1] 0.

Google Scholar

[1] 5 as-spun 5min 15min 120min J (T) H (kA. m-1 ).

Google Scholar