Age Hardening Behavior in Al-8Zn-2Mg-2Cu Wrought Aluminum Alloy

Abstract:

Aluminum alloys based on Al-Zn-Mg-Cu system classified under high strength light alloys, find a large scale application in aerospace sector. In the present study, heat treatment of an Aluminum alloy with Al-8Zn-2Mg-2Cu wt.% (AA7449) was carried out. Heat treatment parameters were optimized based on hardness and conductivity measurements. The mechanisms of strengthening in primary and secondary aged states are explained using hardness and conductivity measurements. Conductivity generally showed an increasing trend with increase in aging time, which could be attributed to decrease in the lattice distortion of the Aluminum matrix with increase in aging time. The dissolution of GP zones and formation of other metastable phases like η’ and stable phase like η were found to reduce the supersaturation in the matrix as the precipitation growth and coarsening processes are completed during overaging. Transmission electron microscopy (TEM) study was carried out to confirm the peak-aging regime. Selected Area Diffraction (SAD) patterns were recorded where GP zones and η’ precipitates were observed in the bright field images to establish their nature. The mechanical properties were correlated with the TEM observations and was suggested that a critical distribution of GP zones and η’ precipitates is essential to achieve peak strength in Al-Zn-Mg alloys.

• Periodical: Materials Science Forum (Volume 710)
• Pages: 527-532
• DOI: https://doi.org/10.4028/www.scientific.net/MSF.710.527
• Online since: January 2012
• Authors: V. Anil Kumar, Raghavendra R. Bhat, Romesh C. Sharma
• Keywords: AA7449, Aging, GP Zones, PFZ, η’ Precipitate

References

[1] P.Liang, T.Tarfa, J.A. Robinson, S.Wagner, P.Ochin, M.G. Harmelin, H.J. Seifert, H.L. Lukas, F.Aldinger, Experimental investigation and thermodynamic calculation of the Al–Mg–Zn system, Thermochemica Acta 314(1,2) (1998) 87-110.

DOI: 10.1016/s0040-6031(97)00458-9

[2] Information on http://lucid.msl.titech.ac.jp /~coe21 /course /pdf /ni_kenkyu_2004 / ogura. pdf.

[3] H.Loffler, I.Kovacs, J.Lendvai, Decomposition processes in Al – Zn - Mg alloys, Journal of Mater. Sci. 18 (1983) 2215-2240.

DOI: 10.1007/bf00541825

[4] L.K. Berg, J.Gjonnes, V.Hansen, X.Z.Li, M.K. Wedel, G.Waterloo, D.Schryvers, L.R. Wallenberg, GP-zones in Al–Zn–Mg alloys and their role in artificial aging, Acta Mater. 49(17) (2001) 3443-3451.

DOI: 10.1016/s1359-6454(01)00251-8

[5] V.Hansen, K.Stiller, G.Waterloo, J.Gjonnes, X.Z.Li, Structures and transformations during artificial aging of an industrial 7xxx-series Al-Zn-Mg-Zr Alloy, Mater. Sci. Forum, 396-402 (2002) 815-820.

DOI: 10.4028/www.scientific.net/msf.396-402.815

[6] N. Ryum, Precipitation kinetics in an Al-Zn-Mg alloy, Z.Metalkd. 66 (1975) 338-343.

DOI: 10.1515/ijmr-1975-660603

[7] R.Ferragut , A.Somoza, A.Tolley, I.Torriani, Precipitation kinetics in Al – Zn – Mg commercial alloys, Journal of Mater. Proc. 141 (2003) 35-40.

DOI: 10.1016/s0924-0136(02)01044-0

[8] Tamas Ungar; The formation of Guinier - Preston zones in the Al - 4.8wt%Zn - 1.2wt%Mg alloy studied by X-ray small angle scattering. Z.MetalKd. 70 (1979) 739-745.

DOI: 10.1515/ijmr-1979-701108

[9] Z.Katz, N.Ryum, Precipitation kinetics in Al-alloys Scripta Metal. 15 (1981) 265-268

DOI: 10.1016/0036-9748(81)90341-0

[10] I.J. Polmear; Light alloys: Metallurgy of Light alloys; 3rd Ed., John Wiley& Sons, 1995.

[11] J.Adrien, E.Maire, R.Estevez, J.C. Ehrstrom, T.Warner, Influence of thermo-mechanical treatment on the microplastic behaviour of a wrought Al–Zn–Mg–Cu alloy, Acta Mater. 52(6) (2004) 1653-1661.

DOI: 10.1016/j.actamat.2003.12.009

[12] R.G. Song, W.Dietzel, B.J. Zhang, W.J. Liu, M.K. Tseng, A.Atrens, Stress corrosion cracking and hydrogen embrittlement of an Al–Zn–Mg–Cu alloy, Acta Mater. 52(16) (2004) 4727-4743.

DOI: 10.1016/j.actamat.2004.06.023

[13] L.F. Mondolfo, Aluminum Alloys : Structure and Properties, 1st Ed., Butterworth and co.Ltd, Boston(MA). 1976.

[14] Tanaka, Hiroki Esaki, Hiroki Minoda, Tadashi, U.S Patent 6,743,308 (2004).

[15] Gang Sha, Alfred Cerezo, Early-stage precipitation in Al – Zn – Mg – Cu alloy (7050) , Acta Mater. 54 (2004) 4503-4516.

DOI: 10.1016/j.actamat.2004.06.025

[16] A.K. Mukhopadhyay, Q.B. Yang , S.R. Singh, The influence of zirconium on the early stages of aging of a ternary Al-Zn-Mg alloy, Acta Metal. et Mater. 42(9) (1994) 3083- 3091.

DOI: 10.1016/0956-7151(94)90406-5