Enhancement of Grain Refinement and Formability of Cross Roll Rolled Ni-10Cr Alloy

Abstract:

This study evaluated the microstructure and mechanical properties enhancement of cross roll rolled Ni-10Cr alloy, comparing with conventional rolled material. Cold rolling was carried out to 90% thickness reduction and subsequently annealed at 700 °C for 30 min to obtain the fully recrystallized microstructure. Particularly, cross roll rolling was carried out at a tilted roll mill condition of 5º from the transverse direction in RD – TD plane. Application of cross roll rolling on Ni-10Cr alloy contributed to the notable grain refinement due to higher effective strain than that of conventional rolling, consequently, average grain size was refined from 135 µm in initial material to 4.2 µm in cross roll rolled material. Furthermore, //ND texture in CRR material was well developed than that of CR material, which contributed to the mechanical properties and formability enhancement.

• Periodical: Materials Science Forum (Volume 761)
• Pages: 95-99
• DOI: https://doi.org/10.4028/www.scientific.net/MSF.761.95
• Online since: July 2013
• Authors: Kuk Hyun Song, Han Sol Kim, Won Yong Kim
• Keywords: Cross Roll Rolling, Formability, Grain Refinement, Mechanical Property, Ni-Cr Alloy

References

[1] K. Neishi, Z. Horita and T.G. Langdon: Mater. Sci. Eng. A Vol. 325 (2002), p.54.

[2] Y. Chino, K. Sassa, A. Kamiya and M. Mabuchi: Mater. Sci. Eng. A Vol. 473 (2007), p.195.

[3] A. Mishra, B.K. Kad, F. Gregori and M.A. Meyers: Acta Mater. Vol. 55 (2007), p.13.

[4] P.Van Houtte, in: C.M. Brakman, P. Jongenburger and E.J. Mittemeijer (Eds.), Proc. ICOTOM7, Netherlands Society for Materials Science, Zwijndrecht, Netherlands, 1984.

[5] D.G. Kim, H.T. Son, D.W. Kim, Y.H. Kim and K.M Lee: J. Alloys Compd. Vol. 509 (2011), p.9413.

[6] K.H. Song, H.S. Kim and W.Y. Kim: Mater. Trans. Vol. 52 (2011), p.1070.