Laser Surface Treatment of SAE 4340 and 300M Steels

Abstract:

The 300M steel has emerged from the high strength SAE 4340 steel, which had been developed in order to obtain increased toughness and weldability in applications requiring better mechanical properties; some minor changes in the alloy elements were introduced: addition of vanadium, and raise in the silicon content. The laser surface hardening is a process in which the steel surface is heated below the melting point, in order to produce solid state phase transformations whithout changing the bulk. This work has evaluated which would be the best parameters for the laser carburizing heat treatment using a low power (50W) CO₂ laser, comparing and contrasting the resulting microstructure and hardness of both steels. The following CO₂ laser parameters were varied: speed, resolution and number of passes; power was kept constant. Carbon black was used as coating. After the surface laser treatment, the samples were cooled in air and the formation of a hardened layer and heat affected zone in both materials was observed. Samples were prepared for metallographic analysis, followed by optical and scanning electron microscopy observation. Layers presented a Vickers hardness value higher than the base metal and the hardened layer had a higher hardness value compared to the heat affect zone. The formation of martensite in the heat affected zone in both steels was observed, although not to the full extension, making this a multiphasic zone.

• Periodical: Materials Science Forum (Volume 805)
• Pages: 204-209
• DOI: https://doi.org/10.4028/www.scientific.net/MSF.805.204
• Online since: September 2014
• Authors: Antonio Jorge Abdalla*, G. de Vasconcelos, A.G. Portela, A.S.M. Cardoso, Carlos Antonio Reis Pereira Baptista
• Keywords: Aeronautic/Aerospace Steels, Laser Carburizing, Surface Treatment

References

[1] A.J. Abdalla, T.M. Hashimoto, C. Moura Neto, M.S. Pereira, N.S. Souza And F.A. Mendes 59º Congresso Anual da Associação Brasileira de Metalurgia e Materiais (ABM). São Paulo, 19 - 22 de Julho 2004. Proceeding.. São Paulo (2004). (SP).

DOI: 10.29381/0103-8559/20213102166-7

[2] R.M. Anazawa: Caracterização mecânica e microestrutural de um aço 300M com microestrutura multifásica. Doutorado (Tese). Guaratinguetá, 2007. Faculdade de Engenharia de Guaratinguetá (FEG/UNESP) (SP).

DOI: 10.1590/s1517-70762008000200019

[3] A.S.M. Cardoso: Caracterização mecânica e microestrutural dos aços SAE 4340 e 300M após soldagem a laser e tratamento superficial de nitretação a plasma Mestrado (Dissertação). Lorena, 2011. Escola de Engenharia de Lorena (EEL/USP). (SP).

DOI: 10.11606/d.97.2011.tde-26092012-143407

[4] E.J.F. Soares: Tratamento superficial a laser dos aços AISI 1045 e AISI 4340: transformações microestruturais. Doutorado (Tese). Campinas, 2005. Universidade Estadual de Campinas (UNICAMP/FEM). (SP).

DOI: 10.47749/t/unicamp.2005.404975

[5] L.F. Assumpção: Otimização de um processo de têmpera por laser em aço 1045. Mestrado (Dissertação). Curitiba, 2009. Universidade Federal do Paraná (UFPR). (PR).

DOI: 10.22239/2317-269x.01620

[6] A.J. Abdalla, T.M. Hashimoto, M.S. Pereira and R.M. Anazawa: Revista Brasileira de Vácuo Vol. 25 p. (2006), p.175.

[7] L.F. Assumpção and A.S.C.M. Oliveira: Têmpera superficial por laser de aço ao chumbo. (Universidade Federal do Paraná, Centro Politécnico Curitiba, 2008).

[8] J., Benedek, A. Shachrai and L. Levin: Case hardening of steel by a CO2 laser beam. (Optics and laser technology, 1980).

DOI: 10.1016/0030-3992(80)90051-1

[9] D.C. Chagas, A. N. Dias, E. F. Antunes and G. Vasconcelos. Aplicação de lubrificantes sólidos (negro de fumo) e tratamento térmico superficial de têmpera em matrizes de aço AISI 4340 via laser CO2, IV SICI - Anais do Seminário Anual de Iniciação Científica e Pós Graduação do IEAv, vol. 1, São José dos Campos, São Paulo, 2010, ISSN 2175-2729.

DOI: 10.20906/cps/sicite2015-0790

[10] R.A. Ganev: Journal of Materials Processing Technology Vol. 121(2002), p.414.

[11] L.C.M. Lavras, J.L. Reis and G. Vasconcelos: 17° Congresso Brasileiro de Ciência dos Materiais (CBECIMAT). Foz do Iguaçu 15-19 de Novembro 2006. Procceding.. Foz do Iguaçu 2006. (PR).

DOI: 10.21041/conpat2019/v2pat260

[12] J.L. Reis: Tratamento térmico superficial do aço AISI M2 via laser de CO2. Mestrado (Dissertação). São José dos Campos, 2009. Instituto Tecnológico de Aeronáutica (ITA/CTA). (SP).

DOI: 10.24849/j.geot.2019..145.03