The goal of this study was to obtain quantitative data about H-penetration through the DN by the measurements of the penetration kinetics at different temperatures.
The points correspond to reduced to unity experimental data values, the solid lines obtained by fitting with the difference of two exponential processes.
The Arrhenius plots derived from the data of the kinetic experiments.
All curves are normalized to the saturation values which were obtained from the data of RBA at 380 K for 3 hours.
Acknowledgments Experimental data presented in this work were obtained using equipment of the Interdisciplinary Recourse Center for Nanotechnology at St.

And they also include data exchange and information sharing between behavior agents through various nodes INTERNET.
The related organizations adopt the uniform data format and the requirement of authority.
You can use WebService-based XML technology to achieve data synchronization.
Meanwhile, it establishes data sharing system and data distribution system.
Osborn：Review of US ESCO industry market trends: an empirical analysis of project data, J.

This temperature range is selected considering thermophysical properties of In and 1-OD listed in Table 1 (obtained from manufacturers’ data sheet and reference articles).
The experimental values obtained are within ± 5% of the reported data from the manufacturer and other sources.
DSC data of 1-OD and NPs-1-OD, CPCM is listed in Table 2.
DSC data of 1-OD and In NPs-1-OD CPCM obtained from experimental studies.
At temperatures 120 ºC and above, reduction of length to diameter aspect ratio of aggregates is observed which leads to a reduction in κ, from 2.56 ± 0.07 W/mk at 110 ºC to 1.68 ± 0.08 W/mk at 140 ºC (shown in Fig. 5).

Due to the slow rotation rate of the cube orientation the resultant 0°/90° ears countervail the newly forming 45° ears up to rather high rolling reductions [5].
Accordingly, the simulated data on texture and strength obtained for the material at intermediate gauge is input into a recrystallization model named AlSoft, which provides information on kinetics of recovery and recrystallization during annealing [14-16], and the resulting texture changes [17].
Symbols indicate experimental data points, thick blue lines are derived by simulation (see text for details).
Accordingly, the simulated data of texture and strength obtained for the material at intermediate gauge was input into the AlSoft recrystallization model, providing information on kinetics of recovery and recrystallization during annealing, and the resulting texture changes.
Fig. 8 shows the softening in form of the evolution of strength and recrystallized volume fraction as a function of annealing temperature, and it appears that the simulation results fit the experimental data points quite well.

The Factor/PCA node provides powerful data-reduction techniques to reduce the complexity of our data.
Example of Data Mining Examining the Data.
Data Preparation.
Data Mining with SQL Server 2008.
Data Mining with SQL Server 2005.

The numerical results were evaluated by direct comparison with experimental data.
This mold outline is required to be able, in laboratory experiments, to determinate the porous media permeability from the experimental data.
Table 2 – Viscosity and permeability data for each experiment.
To validate the simulation obtained with PAM-RTM, the results of the flow front position were compared with experimental data, as shown in Figs. 3, 4 and 5.
c) Numerical results showed good agreement with the experimental data in terms of front flow position, filling time and injection pressure.

Quantitative results (kinetics curves) are obtained by processing the potentiodynamic scanning data with the method in question.
Data pre-processing.
Local binomial regression was performed and original data were replaced by the fitting values during smoothing.
Data were pre-processed before calculation by correcting and smoothing (Fig. 5).
A coverage parameter qp can be define as the coverage value at Ea=Ep, a, which can be acquired in the final data sequences of processing.

"Semantic Retrieval" is determining the specific vocabulary, topic or keyword, it transforms the original data to kernel data further correspond re-late topics, for example people, event, time, location, object.
When the action begins printing, which have three processes is started, including Windows Application and Printing Process as well as Data Extracting.
In data extraction, we can focus on the printing process and after printing the print buffers Spool Directory temporary files in two parts.
Therefore, this study is priority to extract it from the printing process, this process is faster than data access in the print buffers, reliability is higher.
After data ex-traction can be directly for processing or temporary storage to another file directory.

The first one transmits data at the same frequency for uplink and downlink.
The later one transmits data simultaneously on different frequencies.
Then each data set will be sent out by separate antennas.
The data are sent at the same frequency simultaneously.
Hence, the time for sending data is doubly faster

Mechanical properties are around 188 GPa for Young's modulus, 254 MPa 0.2% proof strength, 453 MPa ultimate tensile strength, 26 % elongation, and 45 % reduction of area.
Δa data, appear significant difference.
When JIR curves are available, the fracture resistance KIR curves in plan strain state can be then determined using the equation below IR2 IR 1 J E K ν− = (2) By the test P-∆a data in Fig. 2, resistance JIR-∆a and KIR-∆a curves are given in Fig. 4.
From the data, the specimen scales have few of differences to measure directly the fracture roughness KIQ values in plan strain state.
The fracture roughness, KIC,P-C, at arbitrary P-C levels can be evaluated using formula ( ) ( )[ ]( )rmsIc s1 avIc lg1 lg IC, 10 KntZK CP CP K −+− − − = (3) where lgKIC,av and lgKIC, rms are average value and standard deviation of the test logarithms of fracture roughness KICi data; i=1, 2, …, ns; ns is number of the KIC data.