Abstract: The high resistivity of SiC required for many device applications is achieved by compensating residual donors or acceptors with vanadium or intrinsic defects. This work addresses the defect levels of substitutional vanadium and the positively charged carbon vacancy (VC +) in semiinsulating (SI) SiC. After reviewing the earlier studies related to both defects, the paper focuses on temperature-dependent Hall measurements and photo-induced electron paramagnetic resonance (EPR) experiments of 4H and 6H SI SiC. In vanadium-doped samples, a V3+/4+ level near Ec-1.1 eV (4H) and Ec-0.85 eV (6H) is estimated by a comparison of dark EPR spectra and the activation energy determined from the Hall data, assuming that vanadium controls the Fermi level. In high purity semiinsulating substrates, analysis of time-dependent and steady-state photo-EPR data suggests that the plus-to-neutral transition of the carbon vacancy involves a structural relaxation of about 0.6 eV.

Abstract: A variety of 4H-SiC samples from undoped crystals grown by the physical vapor transport technique have been studied by temperature dependent Hall effect, optical and thermal admittance spectroscopy and thermally stimulated current. In most samples studied the activation energies were in the range 0.9 - 1.6 eV expected for commercial grade HPSI 4H-SiC. However, in several samples from developmental crystals a previously unreported deep level at EC-0.55 ± 0.01 eV was observed. Thermal admittance spectroscopy detected one level with an energy of about 0.53 eV while optical admittance spectroscopy measurements resolved two levels at 0.56 and 0.64 eV. Thermally stimulated current measurements made to study compensated levels in the material detected several peaks at energies in the range 0.2 to 0.6 eV.