Microstructure and Wear Properties of Laser Synthesized Composite Coatings on Ti-6Al-4V

Jin Nan Zhao; Jing Liang; Sui Yuan Chen; C.S. LIU; Feng Hua Liu

doi:10.4028/www.scientific.net/AMM.217-219.1354

Paper Titles

Study on the Control System of Vertical Tin-Plating Process for Semi-Flexible Coaxial Cable
p.1336

Tool Deflection Error Regularization and Compensation in End Milling of Contour Surfaces
p.1341

Study on the Microstructure of FeCrAl/Aluminum Bronze Composite Coatings Prepared by Supersonic Electric Arc-Spraying
p.1346

Microstructure and Wear Resistance of Laser Cladding Nano-Al₂O₃/MCrAlY Composite Graded Coating on TiAl Alloy
p.1350

Microstructure and Wear Properties of Laser Synthesized Composite Coatings on Ti-6Al-4V
p.1354

Investigation on the Interfacial Bonding Strength between Ni-P-W/Al₂O₃ Composite Coatings and NdFeB Matrix
p.1359

Synthesis and Evaluation of Anionic Gemini Surfactant
p.1363

Optimization of Processing Parameters for Electrolysis and Plasma Polishing
p.1368

Springback Prediction Using the Split-Ring Test Based on a Combined Anisotropic Hardening Model
p.1375

HomeApplied Mechanics and MaterialsApplied Mechanics and Materials Vols. 217-219Microstructure and Wear Properties of Laser...

Microstructure and Wear Properties of Laser Synthesized Composite Coatings on Ti-6Al-4V

Abstract:

Ti-6Al-4V, C and TiB2 powders (71.5%Ti-6Al-4V+ 26.2%TiB2+2.3%C in wt. %) were prepasted and then laser clad on Ti-6Al-4V substrates. Laser cladding was carried out with a Nd:YAG pulse laser with the parameters of defocus length 15mm, pulse frequency 15Hz, scanning speed 2-4mm/s, electric current 200-240A. Microstructure and phases were analyzed with the Optical Microscopy(OM), Scanning Electron Microscopy(SEM) and X-Ray Diffraction(XRD). Laser cladding layers with smooth surfaces, good metallurgical bonding with no cracks and pores were formed. The average thickness of the coatings is approximately 80μm. Reactions among Ti, C and TiB2 in the laser molten pool cause in-situ synthesis of TiB, TiB2 and TiC reinforcements. The average microhardness is 836HV, which is more than twice that of the Ti-6Al-4V substrate (320HV). Friction coefficients of the cladding coatings fluctuate between 0.26-0.3. Laser cladding specimen with powder mixture of 71.5%Ti-6Al-4V+ 26.2%TiB2+2.3%C (weight loss 0.0007g after sliding 245m) possesses better wear property than that of the specimen with powder mixture of 90%Ti-6Al-4V+ 10%B4C (weight loss 0.0068g).