Preparation and Properties of Anionic Polymer Emulsion in the Presence of a Reactive Surfactant

Hua Sheng Lu; Zhong Xiao Li; Yu Guang Feng; Jia Ling Pu

doi:10.4028/www.scientific.net/AMM.262.430

Paper Titles

The Application of Gray Associated with Neighborhood Characteristics in the Defect Denoising
p.414

Study on the Technical Conditions of Old Newspaper(ONP)/ Recycled-Polypropylene(rPP) Composites
p.418

Use of Microcapsules of Oregano Essential Oil to Extend the Shelf Life of Strawberries
p.422

Research of the Factor that Influence the Glossiness of Water-Based Tipping Paper Gravure Varnish
p.426

Preparation and Properties of Anionic Polymer Emulsion in the Presence of a Reactive Surfactant
p.430

Application of Water-Based Magnetorheological Fluid in the Production of Stereoscopic Printing Grating
p.435

Study on the Double-Layer Structure Thermal Imaging System
p.440

The Research of Coating Process for Paper-Based Printing Plate
p.444

Synthesis of a Novel Low Dielectric Constant Fluorine Containing Epoxy
p.448

HomeApplied Mechanics and MaterialsApplied Mechanics and Materials Vol. 262Preparation and Properties of Anionic Polymer...

Preparation and Properties of Anionic Polymer Emulsion in the Presence of a Reactive Surfactant

Abstract:

Stable polymer emulsion derived from Butyl Methacrylate (BMA), 4-vinyl pyridine (4-VP), vinylidene chloride (VDC) and divinylbenzene (DVB) with different size and distribution were prepared through soapless emulsion polymerization by using a reactive surfactant and a redox initiator. The influences of the quality ratio of the reactive surfactant to the monomers and the dosages of the cross-linking agent on the stability and thermal properties of the emulsion were studied. The obtained polymer nano-particles have higher ξ potential, and the particle sizes have narrow distribution. This polymerization system can give some further understanding on the mechanism of emulsion polymerization .The solid content of the emulsion could be as high as 40% and the particle sizes could be adjusted in the range of 40-300nm. Otherwise, using infrared spectroscopy, size and ξ analyzer, gravitational thermal analysis and differential scanning calorimeter, properties of the emulsion latex were tested. This kind of latex may have applications in the development of water-developable thermal-sensitive material system.