The Rotational Extrusion Alloying Al-Ti Composite

Article Preview

Abstract:

The Rotating Extrusion Alloying (REA) is a process which combined friction stir welding process and extrusion technology. In the REA process, dissimilar metals are mixed, cracked, and subjected to high speed, severe pressing deformation, and therefore rapidly alloy at a low temperature. The Al-Ti alloy has been prepared by REA. The result shows that during REA process, the original materials and the products after synthesis present high energy ball mill and from sintering the compound are avoided, and the contamination to the compound due to the contact with the surrounding atmosphere and high energy balls disappear. REA technology can be alloyed Al-Ti material. Its phases are mainly composed of Al and Al3Ti, which are distributed more evenly in the aluminum. After heat treatment, its phases’ types and pole figures have no significant change, but there is a trend of transition to the non-equilibrium stable phase. Small-angle grain boundaries decrease or even disappear.

You might also be interested in these eBooks

Info:

Periodical:

Pages:

92-95

Citation:

Online since:

December 2012

Export:

Price:

Permissions CCC:

Permissions PLS:

Сopyright:

© 2013 Trans Tech Publications Ltd. All Rights Reserved

Share:

Citation:

[1] Mao Weiming. Metallic materials crystallographic texture and anisotropy, Science Press, Beijing, (2002)

Google Scholar

[2] Y. Morisada,H. Fujii b,T. Nagaoka K. Nogib,M. Fukusumi. Science Direct composites part A applied sciences and manufacturing, 2007, 38, 2097-2101.

DOI: 10.1016/j.compositesa.2007.07.004

Google Scholar

[3] Z. Y. MA. Metallurgical and Materials Transactions A, 2008, 39A, 642-658.

Google Scholar

[4] Z.Guo, S.E. Lee, H.Kim, S.Park.Et al. Acta materiaialia. 2009, 267-277.

Google Scholar

[5] T.P.D. Rajan, R.M. Pillai, B.C. Pai, Alloys Compd, 2008, 453, 4-L7.

Google Scholar

[6] G. Gonzalez, A. Sagarzazu, D. Bonyuet, L. D. Angelo, Alloys Compd. 2009,483, 289-297.

Google Scholar

[7] I.S. Lee, P.W. Kao, N.J. Ho, Intermetallics ,2008, 16,1104-1108.

Google Scholar

[8] Shafiei-Zarghani A., Kashani-Bozorg S.F., Zarei-Hanzaki A, Mater. Sci. Eng. A , 2009,500,P.84.

Google Scholar

[9] Lim D.K., Shibayanagi T., A.P. Gerlich. Mater. Sci. Eng. A, 2009,507, 194.

Google Scholar

[10] Hu C.M., Lai C.M., Kao P.W., et al. Scripta mater , 2009,60, 639.

Google Scholar

[11] KE Liming, No. 50674056 of National Natural Science Foundation of China.

Google Scholar

[12] Jin Long, Li Jianping, Ke Liming, Xing Li. Journal of Nanchang Hangkong University (Natural Science), 2009, 2, 16-19.

Google Scholar

[13] Zhang Lipan,Ke Liming,Xing Li,Sun Dechao. Journal of Nanchang Hangkong University (Natural Science), 2004, 2, 6-9.

Google Scholar

[14] Ke Liming, Pan Jiluan, Xing Li, Wang Shanlin. Journal of Mechanical Engineering, 2009,4, 17.

Google Scholar