LJ707-Crnimo Flux Cored Wire of Basic Slag System Be Applied to Non-Preheating Welding Technology of HSLA

Abstract:

This article investigates the welded joints of HSLA Q550 without preheating and post-heating treatment process. Tensile test, bending test, low temperature impact test, and the impact fractures and joint microstructure observation and analysis are used.The test result shows that the welded joins achieves equal strength with base metal. The average values of the welded joints impact absorbed energy at-20 °C are greater than 40J and at-40 °C its average values are greater than 27J, thus the low-temperature impact energy joint can meet the service requirements of hydraulic support. It shows that choosing proper welding material, developing reasonable welding and post-heating treatment process can cancel the preheating process of Q550 steel welding.

• Periodical: Applied Mechanics and Materials (Volume 364)
• Pages: 584-588
• DOI: https://doi.org/10.4028/www.scientific.net/AMM.364.584
• Online since: August 2013
• Authors: Tao Gao Hurile, Fu Rong Chen, Yong Fei Hao, Ai Ai Zhang
• Keywords: HSLAQ550, Low-Temperature Impact Toughness, Non-Preheating Welding

References

[1] YANG Daohe, in: Welding Procedure of Q550D Low Alloy Structural Steel on Hydraulic Framework, Coal Technology, 2007, 26(10): 8-10.

[2] CHEN Junwei et al, in: Analysis and Proof of High Intensity Plate Welding Procedure, Modern Manufacturing Technology and Equipment, 2008, 4: 46- 47.

[3] Zhang Lei, LI Yajiang et al, in: Study on welding wire matching of Q690 high-intensity steel used in hydraulic support [J]. Modern Welding, 2010, 1: 21-24.

[4] JIANG Qinglei, LI Yajiang et al, in: Research on microstructure and properties and welding material match of Q550 steel[z]. Science paper Online.

[5] Chen Yuchuan, in: Low-alloy structural steel welding technology [M]. Beijing: CHINA MACHING PRESS, 2008, 6.