Study on Synthesis and Properties of Waterborne Polyurethane Modified by Epoxy Resin

Zhi Ming Jin; Wen Lu Guo; Cai Hua Gao

doi:10.4028/www.scientific.net/AMM.395-396.423

Paper Titles

Study on the Curing Reaction and Rheological Behavior of Bismaleimide Resin
p.407

Synthesis and Polymerization Kinetics of PMMA in [BMIM]BF₆ Imidazolium Ionic Liquids
p.411

Preparation and Research of Polymolybdate/Polymer Composite Membrane by Electrospinning and its Photo-Catalytic Property
p.415

Study on the Poly (ether sulfone) Microfibers
p.419

Study on Synthesis and Properties of Waterborne Polyurethane Modified by Epoxy Resin
p.423

Study of the Parameters of Lightweight Polymer-Cement Repair Mortars Exposed to High Temperatures
p.429

A Comparative Study on Production of Autoclaved Aerated Concrete by Coal Gangue Fly Ash
p.433

Physical Properties of Waste Concrete Recycled Aggregates According to Coating Factor
p.439

Analysis Based on FLAC^3D of Surface Subsidence Caused by a Double-Tube Parallel Tunnel Excavation
p.443

HomeApplied Mechanics and MaterialsApplied Mechanics and Materials Vols. 395-396Study on Synthesis and Properties of Waterborne...

Study on Synthesis and Properties of Waterborne Polyurethane Modified by Epoxy Resin

Abstract:

The waterborne polyurethane (WPU) modified by epoxy resin was synthesized by using isophorone diisocyanate (IPDI), poly propylene glycol (PPG-1000), 2,2-dimethylol propionic acid (DMPA) and epoxy resin as the main raw materials. The WPU properties were characterized by TGA, FTIR, and so on. The study shows that when n_NCO/n_OH=1.4, the mount of DMPA is 5.0%, the emulsifying property of WPU which is modified epoxy resin with high epoxy value is well. And when the mounts of E-20, E-44 are 2.0%, 4.0% respectively, the synthesized emulsion with small size has well stability. The modified WPU which possesses high hardness, low water absorption, good heat resistance and anticorrosion, has a well combination property.