Influence of Heat Treatment for the Microstructure in GCr15 Bearing Steel

Abstract:

The influence of microstructure in GCr15 bearing steel by the different heat treatment conditions was studied, and the influence regular pattern of recrystallization percentage in GCr15 bearing steel by the different deformation amount, deformation temperature and dwell time after rolling was also analyzed. The research results show that when the deformation temperature and deformation amount under certain conditions, the recrystallization percentage of deformed austenite in GCr15 bearing steel increases as the dwell time after rolling increases, and the austenitic grain is also grow up; The uniformity of deformed austenite organization is influenced greatly by the different deformation amount, deformation temperature and dwell time after rolling, when the deformation temperature is 950 °C, the deformation amount is 45% and the dwell time after rolling is 100 S, the recrystallization percentage can up to 84.57%.

• Periodical: Applied Mechanics and Materials (Volumes 44-47)
• Pages: 2385-2389
• DOI: https://doi.org/10.4028/www.scientific.net/AMM.44-47.2385
• Online since: December 2010
• Authors: Fei Ming Xie, Yan Lin Wang, You Yang Xiang, Qing Zhang
• Keywords: GCr15 Bearing Steel, Heat Treatment, Microstructure, Recrystallization

References

[1] W. X. Song: Metallography (Metallurgical industry press, Beijing 1989).

[2] Y. Q. Weng: Iron and Steel. Vol. 40(2005), p.1.

[3] B. L. Guo: Materials Processing Technology. Vol. 74(1998), p.23.

[4] L. J. Zhu, D. Wu and X. M. Zhao: Materials Science and Technology. Vol. 15(2007), p.746.

[5] W. G. Gao, J. W. Liu and Y. X. He: Journal of Hunan Institute of Engineering. Vol. 11(2001), p.39.

[6] D. N. Wang, Y. R. Xing and S. H. Wang: Material and Heat Treatment. Vol. 3(2008), p.64.

[7] Z. Z. Ma: Metal Heat Treatment. Vol. 7(1997), p.20.