6063 Aluminum Alloy Online Quenching Surface Heat Transfer Coefficient and the Temperature Field Simulation

Abstract:

For the 6063 aluminum alloy spray quenching process, respectively establish finite element model of upper, lower nozzle jet impact and water area and meshing in the Gambit. Import into fluent software for cooling numerical simulation, getting the upper and lower nozzle’s pressure contours , velocity contours , heat transfer coefficient curve and water area’s velocity contours and heat transfer coefficient curves. Analysis the various contours and the heat transfer coefficient along the aluminum plate surface radial distribution: upper nozzle’s heat transfer intensity is not in stationary point and near its both sides; Lower nozzle’s contours and heat transfer coefficient has a certain similarity with the upper nozzle, but the maximum heat transfer intensity is at stagnation point; Water area‘s heat transfer coefficient fall faster at the entrance and maintained at a constant value finally. Put heat transfer coefficient as a boundary condition into the ansys software to simulate the three dimensional temperature field of quenching process and analysis the temperature field contours in different time: the biggest speed is 36°C/s during the process of quenching, appearing in the high temperature range, namely deformation sensitive areas, therefore it most likely to occur deformation at the beginning of the quenching profiles.

• Periodical: Applied Mechanics and Materials (Volumes 446-447)
• Pages: 146-150
• DOI: https://doi.org/10.4028/www.scientific.net/AMM.446-447.146
• Online since: November 2013
• Authors: Hui Wang, Hai Bo Yang
• Keywords: 6063 Aluminum Alloy, Ansys Temperature Field Simulation, Heat Transfer Coefficient, Online Quenching

References

[1] Liu J A. The Extrusion of Large Sized Special 6005A Aluminium Profile. Light Alloy Processing Technology, 2004, 2(4): 36-41.

[2] Su H Y. Aircraft, Railway Vehicles and Ships use Aluminum Trend [J]. World Nonferrous Metals, 2010 (4) : 69.

[3] Liu J A, Chen C L, Wang W Q. Aluminum Alloy Forging Production Technology and Forging Application Development [J]. Light Alloy Processing Technology, 2010, 38 (1) : 13 - 18.

[4] Gao Y K, Zhang Z G. Measurement of Residual Stress and Simulation Analysis Method [J]. Failure Analysis and Prevention, 2009, 4 (4) : 251-254.

[5] Dong C J, Wang M K, Sun X T. Research for Reducing Wide Thickness Extrusion Plate's Residual Stress Technology [J]. World Nonferrous Metals, 2009 (11) : 34 and 35.

[6] Gong H, Wu Y X, Liao K. Influence of Residual Stress of Different Quenching Process for 7050 Aluminum Alloy Thick Plate [J]. Journal of Central South University of Technology, 2010, 9 (4) : 1354-1359.

[7] He Y B. Studies on influencial factors of spray cooling of typical aluminum extruded profiles [Dissertation]. Beijing: University of Science and Technology Beijing, 2010: 2.

[8] Shen Y. Experimental Research and Quenching Process Simulation for TNM360 [Dissertation]. Beijing: Beijing University of Science and Technology, (2013).