Research on Secondary Cooling Technology for Billet of HRB500E Vanadium-Containing Steel Rebar

Abstract:

Hot ductility of HRB500E vanadium-containing steel rebar was study with thermal simulation test and the secondary cooling model was established based on the relationship between the cooling water and the casting speed. The solidification cooling curves and the temperature fields of HRB500E were simulated with the PROCAST software. The result of the hot ductility and the pin shooting experiment shows that the casting straightening temperature should be above 902 °C and the secondary cooling model was feasible and accurate. Finally the high-quality billet of HRB500E was obtained.

• Periodical: Applied Mechanics and Materials (Volumes 477-478)
• Pages: 945-948
• DOI: https://doi.org/10.4028/www.scientific.net/AMM.477-478.945
• Online since: December 2013
• Authors: Peng Tian, Zhi Yong Zhong, Rui Guo Bai, Xing Li Zhang, Quan Li Wang, Hai Gao, Xin Guang Hu
• Keywords: Hot Ductility, HRB500E, Secondary Cooling, Vanadium-Containing

References

[1] M David, Li Y, Metallurgical benefits of vanadium micro-alloying in producing high strength seismic grade rebar. Proceedings of International Seminar on Production and Application of High Strength Seismic Grade Rebar Containing Vanadium (Beijing, June 23, 2010): 32.

[2] Peng Tian, Zhiyong Zhong, Ruiguo Bai, et al: Applied Mechanics and Materials, Vol. 357-360 (2013): p.893.

[3] Cao Jin zoei, Feng Liang-hua, Liu Kun, et al: Journal of University of Science and Technology Liaoning, Vol. 32(2): p.134.

[4] Jianfeng Cao, Ke Feng, Zhiwei Han: Advanced Materials Research, Vol. 652-654(2013): p.2441.

[5] Yiwen Kong, Ke Feng, Zhiwei Han, et al: Applied Mechanics and Materials, Vol. 120(2012): p.510.

[6] Jianli Zhang, Yanming Li: Advanced Materials Research, Vol. 268-270(2011): p.1152.