Preparation Technology on Semi-Solid of ZL101
p.1858

Study on Wear Behaviour of Ceramics/1Cr18Ni9Ti Wear Components in H₂O₂ Solution
p.1863

Development of A Two-Equation Turbulence Model for Hypersonic Shock Wave and Turbulent Boundary Layer Interaction
p.1868

Unsteady Characteristics of Breakdown Vortices over Delta Wing
p.1874

Unsteady Aerodynamic Characteristics of a High Speed Train with Crosswind
p.1878

HomeApplied Mechanics and MaterialsApplied Mechanics and Materials Vols. 66-68Preparation Technology on Semi-Solid of ZL101

Preparation Technology on Semi-Solid of ZL101

Abstract:

The semi-solid microstructure of ZL101 alloy was fabricated by technology of vibrating inclined cast. The effections of length of slope and vibration voltage on microstructure were also investigated. The experimental results showed that two parameters played an important role on the microstructure of ZL101 alloy. The homogeneous, small and rounded sphere-like semi-solid equiaxed crystals were obtained when the ZL101 alloy was cast in water-cooled copper mold with 25cm slope length at 640 °C and 60v vibration voltage, the average grain diameter and shape factor of which was 26.5um and 0.8, respectively.

You might also be interested in these eBooks

Mechanical, Materials and Manufacturing Engineering

View Preview

Info:

Periodical:

Applied Mechanics and Materials (Volumes 66-68)

Pages:

1858-1862

DOI:

https://doi.org/10.4028/www.scientific.net/AMM.66-68.1858

Citation:

Cite this paper

Online since:

July 2011

Authors:

Rong Xi Yi, Wen Xian Huang, Zhao Hui Liu, Shi-Kun Xie

Keywords:

Equiaxed Grain, Microstructure, Slope Length, Vibration Voltage, ZL101

Export:

RIS, BibTeX

Price:

Permissions CCC:

Request Permissions

Permissions PLS:

Request Permissions

Сopyright:

Citation:

References

[1] S.K. Xie, X.Q. Zheng, R.X. Yi, et al: Key Engineering Materials, Vol 419(2010), p.517.

Google Scholar

[2] W.L. Wang, X. Lin and W.D. Huang, et al: Foundry Technology Vol. 28 (2007), p.918.

Google Scholar

[3] R.X. Yi, S.K. Xie and X.L. Pan: Ordnance Material Science and Engineering, Vol. 32(2009), p.21.

Google Scholar

[4] H.M. Guo X.J. Yang,B. HuiP: The Chinese Journal of Nonferrous Metals Vol. 14 (2004), p. (2049).

Google Scholar

[5] R.X. Yi, S.K. Xie and X.L. Pan, et al: Hot Working Technology Vol. 38 (2009), p.25.

Google Scholar

[6] X.F. Tian, Z.T. Fan and N.Y. Huang: The Chinese Journal of Nonferrous Metals Vol. 16 (2006), p.1838.

Google Scholar

[7] R.X. Yi, S.K. Xie and X.Q. Zheng: Light Alloy Fabrication Technology Vol. 37 (2009), p.14.

Google Scholar