Experimental Investigations of the High-Temperature Phase Relationship and Ordering Transition in Ni-Mn-Ga Ternary System

Article Preview

Abstract:

The phase equilibria at 900 °C and B2/L21 order-disorder transition in the Ni-Mn-Ga ternary system were investigated by analyzing the equilibrated alloys and diffusion couples using a combination of techniques. It was confirmed that a bcc single phase region exists in a wide composition range at 900 °C, and the critical temperatures of B2/L21 order-disorder transition were determined in Ni-50 at.% section, which exhibits a maximal ordering transition temperature of 796 at Mn content of 25 at.%. The obtained results will be helpful for the preparation and annealing of Ni-Mn-Ga alloys in the specific temperature.

You might also be interested in these eBooks

Info:

Periodical:

Advanced Materials Research (Volumes 148-149)

Pages:

1695-1700

Citation:

Online since:

October 2010

Export:

Price:

Permissions CCC:

Permissions PLS:

Сopyright:

© 2011 Trans Tech Publications Ltd. All Rights Reserved

Share:

Citation:

[1] K. Ullakko, J.K. Huang, C. Kantner, R.C. O'Handley and V.V. Kokorin: Appl. Phys. Lett. Vol. 69 (1996), p. (1966).

Google Scholar

[2] C.B. Jiang, G. Feng and H.B. Xu: Appl. Phys. Lett. Vol. 20 (2002), p.1619.

Google Scholar

[3] J. Pons, V.A. Chernenko, R. Santamarta and E. Cesari: Acta Mater. Vol. 48 (2000), p.3027.

Google Scholar

[4] S.J. Murray, M. Marioni, S.M. Allen, R.C. O'Handley and T.A. Lograsso: Appl. Phys. Lett. Vol. 77 (2000), p.886.

Google Scholar

[5] A. Sozinov, A.A. Likhachev, N. Lanska and K. Ullakko: Appl. Phys. Lett. Vol. 80 (2002), p.1746.

Google Scholar

[6] M.A. Marioni, R.C. O'Handley and S.M. Allen: Appl. Phys. Lett. Vol. 83 (2003), p.3966.

Google Scholar

[7] Y.Q. Ma, C.B. Jiang, Y. Li, H. B Xu, C.P. Wang and X.J. Liu: Acta Mater. Vol. 55 (2007), p.1533.

Google Scholar

[8] H.B. Xu, Y.Q. Ma and C.B. Jiang: Appl. Phys. Lett. Vol. 82 (2003), p.3206.

Google Scholar

[9] Y.Q. Ma, C.B. Jiang. G. Feng and H.B. Xu: Scripta Mater. Vol. 48 (2003), p.365.

Google Scholar

[10] R.W. Overholser, M. Wuttig and D.D. Neumann: Scripta Mater. Vol. 40 (1999), p.1095.

Google Scholar

[11] C. Wedel and K. Itagaki: J Phase Equilibria Vol. 22 (2001), p.324.

Google Scholar

[12] S.M. Hao, K. Ishida and T. Nishizawa: Metall. Trans. A Vol. 15 (1984), p.1819.

Google Scholar

[13] X.J. Liu, C.P. Wang, I. Ohnuma, R. Kainuma and K. Ishida: Metall. Mater. Trans. A Vol. 35 (2004), p.1641.

Google Scholar

[14] X.J. Liu, R. Kainuma, H. Ohtani and K. Ishida: J Alloys Comp. Vol. 235 (1996), p.256.

Google Scholar

[15] S. Hayashi, S.I. Ford, D.J. Young. D.J. Sordelet, M.F. Besser and B. Gleeson: Acta Mater. Vol. 53 (2005), p.3319.

Google Scholar

[16] Y.Q. Ma, S.Y. Yang, C.P. Wang and X.J. Liu: Acta Mater. Vol. 57 (2009), p.3232.

Google Scholar

[17] Y.Q. Ma, L.H. Xu, Y. Li, C.B. Jiang, H.B. Xu and Y.K. Lee: Z Metallkd. Vol. 96 (2005), p.843.

Google Scholar

[18] S.Y. Yang, S.L. Lai, Y.Q. Ma, C.P. Wang and X.J. Liu: submitted to Acta Materiallia (2010).

Google Scholar

[19] C.B. Jiang, Y. Muhammad, L.F. Deng, W. Wu and H.B. Xu: Acta Mater. Vol. 52 (2004), p.2779.

Google Scholar