Surface Inorganic Modification of Wollastonite and its Application in Filling Polypropelyne

Abstract:

Article Preview

Wollastonite was inorganic modificated by coating aluminium silicate with heterogeneous deposition method.SEM, XRD, FTIR, BET surface area analyzer were used to characterize the product. XRD result shows that wollastonite is coated with nano-aluminium silicate. BET result shows that the specific surface area of particles increases by 200%. FTIR result shows that the content of OH group increases.Whiteness test shows that the whiteness increases by 2.0. Application test shows that the polypropelyne(PP) products filled with inorganic modificated powder have superior physical properties or mechanical properties(tensile strength 20.45Mpa, bending strength 38.02Mpa) than that with uncoated wollastonite and pure PP and the heat distortion tempeature increases by 28.6°C than pure PP.Inorganic modification of wollastonite can improve the joint interface between wollastonite and PP.

Info:

Periodical:

Advanced Materials Research (Volumes 154-155)

Edited by:

Zhengyi Jiang, Xianghua Liu and Jinglong Bu

Pages:

50-56

DOI:

10.4028/www.scientific.net/AMR.154-155.50

Citation:

C. L. Wang et al., "Surface Inorganic Modification of Wollastonite and its Application in Filling Polypropelyne", Advanced Materials Research, Vols. 154-155, pp. 50-56, 2011

Online since:

October 2010

Export:

Price:

$35.00

In order to see related information, you need to Login.

In order to see related information, you need to Login.