Effect of Pre-Deformation and Ageing on Compressive Behavior of Ti-58.25wt%Ni Alloys at Room Temperature

Abstract:

Article Preview

In this paper, effect of pre-deformation and ageing on compressive behavior of Ti-58.25wt%Ni was investigated at room temperature. Through range analysis of three factors and three levels on transformation temperature measured by DSC, ageing at 673K enhanced phase transformation temperature obviously, the As temperature could reach 308.02K. Transformations of B2-B19’ and B2-R-B19’ appeared after the treatments. Saw tooth shape phenomenon on the loading curves indicating the typical martensitic transformation was also observed. Dynamic balance due to compatible action among various phase under increased load kept the slope of the loading curves constantly. Pre-deformation by 0.2% resulted in higher compressibility (4.9%), and ageing at 523K caused better recovery (95.4%).

Info:

Periodical:

Advanced Materials Research (Volumes 197-198)

Edited by:

Huaiying Zhou, Tianlong Gu, Daoguo Yang, Zhengyi Jiang, Jianmin Zeng

Pages:

375-382

Citation:

S. C. Zhu et al., "Effect of Pre-Deformation and Ageing on Compressive Behavior of Ti-58.25wt%Ni Alloys at Room Temperature", Advanced Materials Research, Vols. 197-198, pp. 375-382, 2011

Online since:

February 2011

Export:

Price:

$38.00

[1] D.Z. Yang: Biomedical Applications of Ni-Ti shape Memory Alloys (Metallurgical Industry Press, China 2003, in Chinese).

[2] L.C. Zhao: Shape Memory Effect and Superelasticity in Alloys (National Defence Industry Press, China 2002, in Chinese).

[3] Y. Takagi, T. Tatsuoka and S. Toshiyuki: Asme. PVRC. Conference, Canada (2007).

[4] T. Tatsuoka, Y. Takagi and S. Toshiyuki: Asme. PVRC. Conference, US (2004).

[5] K. Gall, H. Sehitoglu and Y.I. Chumlyakov: Acta Metall. Vol. 47 (1999), p.1023.

[6] L. Yong, Z. Xie and J.V. Humbeeck: Acta Metall. Vol. 46 (1998), p.4325.

[7] R.A. Raghavendra, F.C. Jiang and S.V. Kenneth: Acta Metall. Vol. 54 (2006), p.4609.

[8] R.A. Raghavendra, F.C. Jiang and S.V. Kenneth: Mater. Sci. A. (2010), p.1665.

[9] H.X. Zhou, S.N. Lv and G.Z. Li: Journal of Naval Aeronautical Engineering Institute, Vol. 23 (2008), p.701, in Cinese.

[10] X.W. Huang, H.B. Yang and G.N. Dong: Titanium Industry Progress. Vol. 21 (2004), p.25, in Chinese.

[11] S.Q. Qian, J.S. Wu: Hot Working Technology. 2 (2005), p.12, in Chinese.

[12] ASTM F36-99 (2003).