Preparation of a New Water-Based Strippable Protected Coating

Abstract:

Article Preview

A new water-based strippable protected coating was made by polyurethane emulsion and nano-CaCO3 was put in the coating as the fillers. The influence of nano-CaCO3 on the coating was discussed and the influence of film thickness on the coating was studied. The performance of the coating was tested, and when the dosage of nano-CaCO3 was 2% and the film thickness was 0.13~0.14mm, the film had the best strippable ability. Its average mechanics intensity was 5.72MPa and average elongation at break was 258.35%.

Info:

Periodical:

Advanced Materials Research (Volumes 239-242)

Edited by:

Zhong Cao, Xueqiang Cao, Lixian Sun, Yinghe He

Pages:

2646-2649

DOI:

10.4028/www.scientific.net/AMR.239-242.2646

Citation:

H. Y. Liu and S. Zhang, "Preparation of a New Water-Based Strippable Protected Coating", Advanced Materials Research, Vols. 239-242, pp. 2646-2649, 2011

Online since:

May 2011

Export:

Price:

$35.00

In order to see related information, you need to Login.

In order to see related information, you need to Login.