Effect of Brazing Clearance on Microstructure and Strength of Welded Joint of 316L Stainless Steel

Zhuo Jun Chen; Ming Wang; Long Long Feng

doi:10.4028/www.scientific.net/AMR.399-401.1890

Paper Titles

Directional Solidification Microsegregation and Concentration Analysis with Different Supersaturation
p.1866

Study on Hot Processing Maps and Flow Instability of 1235 Al Alloy Treated by Different Methods of Purification
p.1870

The Effect of Active Packaging Film on the Quality of Dashehari Mango Fruits
p.1881

Performance Evaluation of SHY-99 Coating for Carbon Steel Water-Cooler
p.1886

Effect of Brazing Clearance on Microstructure and Strength of Welded Joint of 316L Stainless Steel
p.1890

Preparation and Characterization of Paclitaxel Imprinted Silica Nanoparticles
p.1894

Effect of Negative Bias Voltage on Corrosion Resistance of TiN Coating Deposited by MAIP
p.1898

Nb-C Alloyed Layer Prepared on TiAl Alloys by Plasma Treatments and its First-Principles Investigation
p.1903

Characteristics of Surface and Interface of Mercury-Stannum Reactive Wetting at Room Temperature
p.1909

HomeAdvanced Materials ResearchAdvanced Materials Research Vols. 399-401Effect of Brazing Clearance on Microstructure and...

Effect of Brazing Clearance on Microstructure and Strength of Welded Joint of 316L Stainless Steel

Abstract:

To study the effect of brazing clearance and temperature on strength and microstructure, vacuum brazing of 316L stainless steel was carried out with BNi-2 nickel-based solder. Choose the different brazing clearance to be processed at 1070°C, analyzed the welding tissue by SEM and XRD, and found that hardness has been greatly improved to 664HV. The results showed that when the 316L stainless steel was brazed with BNi-2 filler metal at 1070°C, the structures of the welded joint were composed of FeNi3, Fe5C2, Cr5FeB3 metallic compounds and solid solutions. The microhardness of the welded joint by the center to both sides had a W-type distribution. When the width of the welded joint was 40μm, the microharedness of the center welded joint was lower than others, and shear strength of this clearance was the highest, about 300MPa.

You might also be interested in these eBooks

New Materials, Applications and Processes

View Preview

Info:

Periodical:

Advanced Materials Research (Volumes 399-401)

Pages:

1890-1893

DOI:

https://doi.org/10.4028/www.scientific.net/AMR.399-401.1890

Citation:

Cite this paper

Online since:

November 2011

Authors:

Zhuo Jun Chen, Ming Wang, Long Long Feng

Keywords:

Brazing Clearance, Brazing Temperature, Stainless Steel (SS), Vacuum Brazing

Export:

RIS, BibTeX

Price:

Permissions CCC:

Request Permissions

Permissions PLS:

Request Permissions

Сopyright:

Citation:

References

[1] Jianyong Zhu, Xuanhui Qu, Huosheng He. The Performance of the Solder Powder BNi2 [J].Hunan metallurgy, 2004, (6): 6-9. In Chinese.

Google Scholar

[2] OUCL, LIAW D W, DU YC. Brazing of 422 stainless steel using the AWS classification BNi-2 braze alloy [J].Journal of Materials Science, 2006, 41(19):6353-6361.

DOI: 10.1007/s10853-006-0709-0

Google Scholar

[3] QiYun Zhang, HongShou Zhuang. Brazing manual [M]. Beijing: Mechanical Industry Press, 1998.

Google Scholar

[4] Jianmin Chen. Study on law of compounds phase in the clearance of BNi-2 vacuum brazing stainless[J]. Journal of Oil University, 2000, (5): 80-83. In Chinese.

Google Scholar

[5] WU X W,CHNADEL R S,SEOW H P, et al. Wide gap brazing of stainless steel to nickel-based superalloy[J].Journal of Materials Processing Technology,2001,113(1):215-221. In Chinese.

DOI: 10.1016/s0924-0136(01)00596-9

Google Scholar

[6] JianMin Chen, ChangFu Zhu. Vacuum Brazing Stainless Steel fittings of Clearance Organization and Phase Composition Characteristics [J]. Journal of Petroleum University, 1999, 23(2):66-68. In Chinese.

Google Scholar