Advanced Materials Research Vol. 409

Abstract: In the present study, microstructure investigation of aluminide coatings after platinum modification deposited by CVD method on Inconel 713 LC Ni-base superalloys were performed. The platinum coatings 3 and 7 m thick were deposited by electroplating process. The diffusion treatment of platinum electroplating coatings at the temperature 1050 °C was carried out for 2h. The low-activity CVD aluminizing of heat treated coatings at the temperature 1050 °C was conducted for 8 h. On the grounds of the obtained results it was found that microstructure of diffusion treated platinum electroplating coatings 3 m and 7 m thick consisted of two phases: γ-Ni and (Al0.25Pt0.75)Ni3. The low activity CVD aluminizing of diffusion treated platinum electroplating coatings 3 and 7 m thick enables the diffusion coating obtaining. The main constituent of aluminide coatings was (Ni,Pt)Al phase.