Fabrication of Bi-2223 Powders Using Sol-Gel Method

Abstract:

The Bi-2223 powders were fabricated by the sol-gel technique. Metal nitrates were used as starting materials, and ethylenediamineteracetic acid was used as chelating agent. The solution was heated until it turns to gel. Then the organic was removed at a temperature of 240°C, and the nitrite was removed at 500°C. The powder was calcined at different temperature, varying the dwelling time. Experimental results show that the main phase of samples after heat treatment is Bi-2212 phase.

• Periodical: Advanced Materials Research (Volume 412)
• Pages: 125-128
• DOI: https://doi.org/10.4028/www.scientific.net/AMR.412.125
• Online since: November 2011
• Authors: Ming Ya Li, Xiao Yan Wang, Cheng Li Ye, Feng Lin Xue
• Keywords: Bi-2223 Powders, Heat Treatment, Sol-Gel Method

References

[1] Z. Han, P.S. Hansen and T. Freltoft: Supercond. Sci. Technol. Vol. 10 (1997), p.371.

[2] J. Jiang and J.S. Abell: Supercond. Sci. Technol. Vol 10 (1997), p.678.

[3] M.Y. Li and Z. Han: Supercond. Sci. Technol. Vol. 20 (2007), p.843.

[4] X.P. Chen, J.C. Grivel, M.Y. Li, et al.: Physica C Vol. 406 (2004), p.176.

[5] V. Rouessac, J. Provost and G. Desgardin: J. Mat. Sci. Vol. 31 (1995), p.3387.

[6] V. Beilin, M. Schieber, Y. Yaroslavsky, et al.: IEEE Trans. Appl. Supercond. Vol. 5 (1995), p.1263.

[7] F.H. Chen, H.S. Koo and T.Y. Tseng: J. Mat. Sci. Vol. 25 (1990), p.3338.

[8] J.H. Greenberg, L. Ben-Dor and H. Selig: J. Therm. Anal. Vol. 50 (1997), p.105.

[9] A. Tampieri, G. Celotti, S. Lesca, et al.: J. Euro. Ceram. Soc. Vol. 20 (2000), p.119.