Near-Infrared Emissions of Sm³⁺ in Li₂O-K₂O-BaO-PbO-Bi₂O₃-Ga₂O₃ Glasses

Abstract:

μNear-infrared (NIR) emissions have been observed in Sm³⁺ doped low phonon energy heavy-metal-gallate glasses. The full-widths at half-maximum (FWHMs) of three fluorescence bands peaking at 960, 1038, and 1185 nm were derived to be 31, 36, and 42 nm, respectively, and the spontaneous transition probabilities were calculated to be 66, 16, and 6 s^-1. Maximum stimulated emission cross-sections ( σ_em) for NIR transition emissions were obtained to be 4.22´10^-22, 1.37´10^-22, and 0.71´10^-22 cm², respectively. Investigations on multi-channel NIR transition emissions of Sm³⁺, especially on the ~1.19 μm emission, which lies in the low-loss wavelength region of transmission window, are beneficial for potential applications in infrared optoelectronic devices.

• Periodical: Advanced Materials Research (Volumes 476-478)
• Pages: 1121-1124
• DOI: https://doi.org/10.4028/www.scientific.net/AMR.476-478.1121
• Online since: February 2012
• Authors: Xiang Ling Zhang, Ming Liu, Xin Zhao, Hai Lin
• Keywords: Heavy-Metal-Gallate Glasses, Near-Infrared Emissions, Samarium Ion

References

[1] X. Wang, X. Yan and C. Kan: J. Lumin. Vol. 131 (2011), p.2325

[2] S. Xu, Z. Yang, G. Wang, J. Zhang, S. Dai, L. Hu and Z. Jiang: Spectrochim. Acta. Part A Vol. 60 (2004), p.3025

[3] D.D. Chen, Y.H. Liu, Q.Y. Zhang, Z.D. Deng and Z.H. Jiang: Mater. Chem. Phys. Vol. 90 (2005), p.78

[4] F. Song, Z. Cheng, C. Zou, Lin. H, X. Yu, J. Zhang, X. Jiang, P. Han and J. Tian: Appl. Phys. Lett. Vol. 93 (2008), p.091108

[5] P. Li, L. Pang, Z. Wang, Z. Yang, Q. Guo. and X. Li: J. Alloys. Compd. Vol. 478 (2009), p.813

[6] J. Zhang, D.L. Yang, E.Y.B. Pun, H. Gong and H. Lin: J. Appl. Phys. Vol. 107 (2010), p.123111