Effect of Corrosion Inhibition on the Stress Corrosion Cracking of UNS S31603 Austenitic Stainless Steel

Abstract:

Brine recirculation pumps are essential components used for circulation of brine in multi-stage flashing chambers desalination plants. Failure of these pumps would result in shutdown of the desalination plants. The rotating parts of these pumps (shaft and impeller) are usually made out of stainless steels or Duplex stainless steels. The pressure parts (casings) are usually made out of Ni-resist ductile irons (NDI). In recent years there have been a number of cases in which NDI casing materials failed by stress corrosion cracking (SCC) especially in the Arabian Gulf region. This makes re-evaluation and further studies on the performance of these materials of paramount importance due to process-related economic and reliability considerations. As possible substitutes to NDI casing materials, the authors of this research have recently published material demonstrating the superiority of the SCC resistance of the super DSS, UNS S32750, over the ASS, UNS S31603, in hot brine environment. Economically, the idea of using chemical corrosion inhibitors to enhance the SCC resistance of the ASS, UNS S31603, is appealing, non famous and worth looking at. In this work the effect of corrosion inhibition on the corrosion resistance and SCC of the ASS, UNS S31603, in hot brine environment, is investigated. Brine water was injected with typical treat rate of 350 ppm of passivating type commercially available Molybdate corrosion inhibitor. Theoretically the corrosion inhibitor was proposed to improve the corrosion resistance of ASS, UNS S31603, in brine solution. Electrochemical polarization measurements and SCC tests were used to evaluate the performance of the metal under inhibited and uninhibited environments. Results have shown that treating the brine with this particular type of inhibitor under this particular treat rate and test conditions increased the pitting tendency of the ASS, UNS S31603. Results from both SCC tests and electrochemical measurements are in agreement and both role out the possibility of enhancing corrosion resistance and SCC of ASS UNS S31603 using Molybdate inhibitor.

• Periodical: Advanced Materials Research (Volumes 476-478)
• Pages: 256-262
• DOI: https://doi.org/10.4028/www.scientific.net/AMR.476-478.256
• Online since: February 2012
• Authors: O.A. Abuzeid, A.I. Aljoboury, M. Abou Zour
• Keywords: Corrosion Inhibition, Desalination Plants, Molybdate Corrosion Inhibitor, Stress Corrosion Cracking (SCC), UNS S31603 Austenitic Stainless Steel

References

[1] Y.A. Alzafin, A-HI. Mourad, M . Abou Zour, O.A .Abuzeid, A study on the failure of pump casings made of ductile Ni-resist cast irons used in desalination plants, Eng Fail Anal. 14(7) (2007), 1294- 1300.

DOI: 10.1016/j.engfailanal.2006.11.040

[2] Y.A. Alzafin, A-HI. Mourad, M . Abou Zour, O.A .Abuzeid, Stress corrosion cracking of Ni-resist ductile iron used in manufacturing brine circulating pumps of desalination plants, Eng Fail Anal. 16(3) (2009), 733- 739.

DOI: 10.1016/j.engfailanal.2008.06.013

[3] ASTM Standard A 439. (2003).

[4] BS Standard 3468. (1986).

[5] Private communication with pump manufacturer. (2007).

[6] ASTM A 240. (2006).

[7] Private communication with the Vice President – Plant 1 (D, E and G), Generation Division, Dubai Electricity and Water Authority, The United Arab Emirates. (2010).

[8] A. I. Aljoboury, A-HI. Mourad, A . Alawar, M . Abou Zour, O.A .Abuzeid, Stress corrosion cracking of stainless steels recommended for building brine recirculation pumps, Eng Fail Anal. 17(6) (2010),1337- 1344.

DOI: 10.1016/j.engfailanal.2010.03.008

[9] E. Flick, Corrosion Inhibitors :An Industrial Guide, second edition, New Jersey: Noyes Publications. (1993).

[10] R. Nishimura and Sundjono, Effect of Chromate and Molybdate on stress corrosion cracking of type 304 austenitic stainless steel in Hydrochloric acid solution, Corrosion. 56 (2000), 361-370.

DOI: 10.5006/1.3280539

[11] A. Devasenapathi and V. S. Raja, Effect of externally added Molybdate on repassivation and SCC behavior of AISI 304 SS in 1M HCl, Corrosion. 52 (1996), 243-249.

DOI: 10.5006/1.3293636

[12] Mill Test Reports. Provided by Industeel, the material manufacturer. (2007).

[13] Metallurgical Test Report. Provided by North American Stainless, the material manufacturer. (2007).

[14] ANSI/ NACE Standard TM0177. (1996).

[15] ASTM Standard G49-85. (2000).

[16] ASTM A370-07. (2007).