Cellular Automaton Simulation and Experimental Observation of the Dynamic Recrystallization of Titanium Alloy TC11 with Varied Strain Rates

Article Preview

Abstract:

During the metal hot working process, the dislocation density will vary with strain and strain rate, and the variation of the dislocation density will affect the grain evolution subsequently. The cellular automaton (CA) method is an effective technique used to simulate the grain evolution of materials. In this work, a dynamic recrystallization (DRX) model of titanium alloy TC11 under varied strain rates was established by the use of cellular automaton method and verified by experimental observation. Two types of loading processes called “begin fast and then slowly” and “begin slowly and then fast” were simulated to investigate the titanium alloy TC11 grain evolution processes during hot working. The simulation results are in good coincidence with experimental data. Both cellular automaton simulation and experimental results show that the flow stresses and DRX transformation percentage during hot working process of the TC11 alloy are closely related not only to the strain rate but also to the loading sequence. Compared to the “begin slowly and then fast” loading sequence, the flow stress with the “begin fast and then slowly” loading sequence is relatively smaller under the same strain rates, and the DRX transformation percentage is relatively larger.

You might also be interested in these eBooks

Info:

Periodical:

Advanced Materials Research (Volumes 476-478)

Pages:

71-74

Citation:

Online since:

February 2012

Export:

Price:

Permissions CCC:

Permissions PLS:

Сopyright:

© 2012 Trans Tech Publications Ltd. All Rights Reserved

Share:

Citation:

[1] R. DING and Z. X. GUO. Acta mater. 49 (2001). p.3163–3175

Google Scholar

[2] R. DING and Z. X. GUO. Computational Materials Science 23 (2002). p.209–218

Google Scholar

[3] R. DING and Z. X. GUO. Materials Science and Engineering. A365 (2004). p.172–179

Google Scholar

[4] G. Kugler , R. Turk. Acta Materialia, 52 (2004). p.4659–4668

Google Scholar

[5] He Yan, Zhang Li-wen, Niu Jin, etc. Transactions of Materials and Heattreatmen, vol26, no.4, August (2005), pp.120-125

Google Scholar

[6] J.W.ZHAO, H.DING, W.J.ZHAO, etc. Acta Metallurgica Sinica (English letters), vol21, no.4, August (2008 ), pp.260-268

Google Scholar

[7] Zhang Li-wen, Lu Yu, Deng Xiao-hu, etc. Journal of Dalian University of Technology, vol48, no.3, May (2008), pp.351-355

Google Scholar

[8] Chen Hui-qin, Cao Chun-xiao, Guo Ling, etc. Journal of Materials engineering, 2009(5), pp.43-48

Google Scholar

[9] Zhaoyang Jin , Zhenshan Cui. J. Mater. Sci. Technol., 2010, 26(12), pp.1063-1070

Google Scholar

[10] Goetz R L, Seetharaman V. Scripta Mater, 1998, 38, pp.405-413

Google Scholar