Experimental Investigation on Water Miscible Rolling Lubricant J4

Abstract:

A contrast test was done about the service performance of commercial emulsion II and water miscible rolling lubricant J4 with polyethylene glycol. The test results were given to have analysed them in lubrication, extreme pressure performance, simulating annealing, resistance of putrefy, rust protection etc. From the rolling mill in the lab, at the same depress ratio, the pressure reduce 3.85kN using J4 than using II, and the rolling power reduce 0.04kW using J4 than using II. By four-ball tester, the maximum load PB of J4 is 932N, the friction is 0.0518, and the wear diameter is 0.47mm. Water miscible rolling lubricant J4 is notable in lubrication, extreme pressure performance, annealing, resistance of putrefy and rust protection. The results may offer the reference for further optimization on water miscible rolling lubricant.

• Periodical: Advanced Materials Research (Volume 499)
• Pages: 376-379
• DOI: https://doi.org/10.4028/www.scientific.net/AMR.499.376
• Online since: April 2012
• Authors: Xing Dong Peng
• Keywords: Polyethylene Glycol (PEG), Rolling Technology Lubrication, Water Miscible Rolling Lubricant

References

[1] J.L. Sun. Rolling Technology Lubricating Principle, Technique and Application (Metallurgical industry Publications, China 2010). (In Chinese).

[2] B. Zhang: Tribology Vol. 31 (2011), p.194(In Chinese).

[3] Z. Wang, X. Wang: Mater. Pro. Technology Vol. 113 (2001), p.659(In Chinese).

[4] W.X. Huang. Application Guide of Lubricant Additive(Petrification industry Publications, China 2003). (In Chinese).

[5] Y.H. Zhou, G.L. Zhou. Metal Processing Anti-friction Material(Petrification industry Publications, China 1997). (In Chinese).

[6] J.L. Dai. Reproduction of Waste Lubricant(Petrification industry Publications, China1999). (In Chinese).