Syntheses and Evaluation of Copolymer 6-Aminohexanoic Acid and 4R-Hydroxy-L-Proline for Bone Repair

Abstract:

A novel synthetic copolymer (PAA) for bone repair was prepared by melt condensation polymerization with 6-aminohexanoic acid (He) and 4R-hydroxy-L-proline (Hyp). The structure and thermal property were characterized by infrared spectrometer (IR), nuclear magnetic resonance (H1NMR) and differential scanning calorimeter (DSC). The results indicated that the PAA had amide linkages in their polymer chains. The Tg of PAA was 57.56°C and significantly higher than that of nylon6, 50.46°C. Meanwhile, the intrinsic viscosity and mechanical properties were investigated at different He/Hyp ratios. It revealed that appropriate introduction of Hyp group could control the degree of polycondensation and adjusted mechanical properties of PAA obviously close to natural bone. The prepared polymers had about 2.12~18.21 % weight loss after 8-week soaking in PBS, showed degradable properties which was essentials to new bone growth. The copolymer of He and Hyp with ratios of 90/10 had 6.57 % weight loss and maintained the yield compressive strengths with about 67.51 MPa after 8 weeks, which exhibited a compatible mechanical properties and degradation speed for bone repair.

• Periodical: Advanced Materials Research (Volumes 562-564)
• Pages: 506-511
• DOI: https://doi.org/10.4028/www.scientific.net/AMR.562-564.506
• Online since: August 2012
• Authors: Jia Chun Jiang, Zhi Tong Zhao, Guo Yu Lv, Yong Gang Yan, Deng Xue Wu
• Keywords: 4R-Hydroxy-L-Proline, 6-Aminohexanoic Acid, Bone Repair, In Vitro Degradation, Mechanical Property, Poly(amino acid)

References

[1] H. Kienapfel MD, C. Sprey MD, A. Wilke MD, P. Griss MD: J. Arthroplasty, Vol. 14 (1999), P. 355.

DOI: 10.1016/s0883-5403(99)90063-3

[2] D.L. Shi: Introduction to Biomaterials (Tsinghua University Press, China, 2005).

[3] M. Vallet-Regí : C. R. Chimie, Vol. 13 (2010), P. 174.

[4] J. Wei, F. Chen, J.W. Shin, H. Hong, C. Dai, C. Su, C. Liu: Biomaterials, Vol. 30 (2009), P. 1080.

[5] L. Nair, C. Laurencin: Prog. Polym. Sci., Vol. 32 (2007), P. 762.

[6] S.M. Kurtz, J.N. Devine: Biomaterials, Vol. 28 (2007), P. 4845.

[7] W. Zhang: Ploym. Bull., Vol. 60 (2008), P. 323.

[8] W. Zhang, J. Shao: J. Polym. Environ., Vol. 19 (2011), P. 177.

[9] C.C. Verheyen, J.R. Wijn, C.A. Blitterswijk, K. Groot: J. Biomed. Mater. Res., Vol. 26 (1992), P. 1277.

[10] K.L. Curtis, J. Fawcett, S. Handa: Tetrahedron Lett., Vol. 46 (2005), P. 5297.

[11] Y.G. Yan, H. Li, G.Y. Lv, X. Cao, Y.F. Wang, A.P. Yang, X. M. Luo, H. X. Pei, Y. M. Song, H. Duan: China patent (2009) No. 101342384A.

[12] A.E. Bozdogan: Polymer, Vol. 45 (2004), P. 6415.