The Effect of Cooling Rate in Molten Salt Electro-Carburisation Process

Abstract:

In the recent development of a new process of electro-carburisation of mild steel in 800 °C molten carbonate based salts, further investigation has been carried out to study the effects of the cooling rate after the electro-carburisation process. In the process, the mild steel to be carburised was made the cathode and an inert SnO2 as anode. Salt mixture of Na2CO3-NaCl (mole ratio 4:1) was used as the electrolyte, and the process was carried out at voltage range of 1.0 to 2.5 V for 60 minutes, and thereafter cooled at certain rate. As revealed by the optical microscopy, the microstructural changes in samples that have been electro-carburised and thereafter cooled either rapidly or naturally in air, were featured by the increase of the carbon rich in the martensite structure at the expense of the original ferrite phase near the surface of the samples. Micro-hardness profiles measured from the surface to the centre of the electro-carburised sample presented clear evidence of carbon penetration as a function of the electrolysis voltage, and significant effects of cooling rate after the electro-carburisation process.

• Periodical: Advanced Materials Research (Volume 576)
• Pages: 264-267
• DOI: https://doi.org/10.4028/www.scientific.net/AMR.576.264
• Online since: October 2012
• Authors: Nancy J. Siambun, Willey Y.H. Liew, George Z. Chen, Daniel A. Jewell, Yeo K. Beng
• Keywords: Electro-Carburisation, Martensite, Microhardness, Molten Salt, Quenched

References

[1] J.R. Davis, Proc. Selection Guide in Surface Hardening of Steels: Understanding the Basics, ASM Int. Ohio, (2002).

[2] P.W. Shimer, US Patent 1, 279, 457. (1918).

[3] R.W. Foreman, G.P. Dupal, and C.R. Fox, US Patent 4, 153, 481 (1977).

[4] W.C. Jones, K.R. Britt, and I.L. Newell, US Patent 4, 591, 397 (1986).

[5] A. Raman, Material Processing: Surface Treatment and Case Hardening. Material Selection and Applications in Mechanical Engineering, Industrial Press, New York, (2007).

[6] N.J. Siambun, H. Mohamed,D. Hu,D. Jewell, K.B. Beng and G.Z. Chen, J. Eletrochem. Soc. 158 (11) (2011)A1-A8.

[7] T. Lyman, Metals Handbook, 8: Metallography, Struc. and Phase Diagrams, 8ed., ASM Int., Ohio, (1985).

[8] D.R. Sadoway, JOM. 53 (2001) 34.

[9] K.T. Kilby, S. Q. Jiao, and D. J. Fray, Electrochim. Acta. 55 (2010) 7126.

[10] L. Dillinger, Etching, 18, Leco Corporation, Michigan, (2002).