The High Temperature Stability of Asphalt Composite Reinforced by Basalt Glass Powder and Basalt Fiber

Abstract:

Wood fiber and lime rock powder have been used as the asphalt stabilizer and filler in highway construction. Basalt fiber and glass powder were adopted as the replacements of traditional stabilizer and filler. The experimental samples were made by tyre rubber powder modified asphalt mixture, basalt fiber, lime stone powder and basalt glass powder. The dynamic stability of the samples at 60 oC was indexed by the runs of automobile tracking. The samples with lime rock powder had the basalt fiber contents 0%, 0.2%, 0.25% and 0.3%, respectively. The corresponding dynamic stabilities were 4500 run/mm, 5300run/mm, >6000 run/mm and 5400run/mm. The samples with basalt glass powder had the basalt fiber contents 0%, 0.2% and 0.25%, respectively. The dynamic stability went above the upper limit of the tester when the basalt fiber content was 0.2%. The control group of basalt glass powder modified sample had 5600run/mm, whereas the control group of lime rock modified sample was 4500run/mm, of which the increment was 24%. We may conclude that the effect of basalt fiber reinforcement was significant. In addition, the basalt glass powder is better than lime rock powder, as the filler of asphalt composite.

• Periodical: Advanced Materials Research (Volume 627)
• Pages: 813-815
• DOI: https://doi.org/10.4028/www.scientific.net/AMR.627.813
• Online since: December 2012
• Authors: Jian Li Lou, Hua Wu Liu, Ai Yun Pang, Han Sun, Shu Wei Yang, Tian Yang Yang
• Keywords: Basalt Fiber (BF), Basalt Glass Powder, High Temperature Stability, Modified Asphalt

References

[1] Dj.M. Maric, P.F. Meier and S.K. Estreicher: Mater. Sci. Forum Vol. 83-87 (1992), p.119

[2] M.A. Green: High Efficiency Silicon Solar Cells (Trans Tech Publications, Switzerland 1987).

[3] Y. Mishing, in: Diffusion Processes in Advanced Technological Materials, edtied by D. Gupta Noyes Publications/William Andrew Publising, Norwich, NY (2004), in press.

[4] G. Henkelman, G.Johannesson and H. Jónsson, in: Theoretical Methods in Condensed Phase Chemistry, edited by S.D. Schwartz, volume 5 of Progress in Theoretical Chemistry and Physics, chapter, 10, Kluwer Academic Publishers (2000).

[5] R.J. Ong, J.T. Dawley and P.G. Clem: submitted to Journal of Materials Research (2003)

[6] P.G. Clem, M. Rodriguez, J.A. Voigt and C.S. Ashley, U.S. Patent 6,231,666. (2001)