Natural Rubber-Toughened Polystyrene: Effects of Mixing Procedure and Maleic Anhydride Content on Impact Property and Phase Morphology

Abstract:

The toughening of polystyrene (PS) by melt blending with natural rubber (NR) was prepared in a brabender plasticorder. Two kinds of processing had been used: (a) one-step mixing in which the three components of PS (60 wt%), NR (40 wt%) and maleic anhydride (MA) were simultaneously introduced in the mixer; (b) two-step mixing in which NR and MA were separately premixed before the final mixing with PS. The effect of MA loading (3 and 5 phr) on gel content, impact energy and morphology of PS-NR-MA blend were further investigated. The results showed that the incorporation of NR into PS increased the impact energy of the blend. The results also showed a significant effect of the different mixing procedures on the properties of PS-NR-MA blend. High contents of unreacted MA and gel were found in the blend obtained by the one-step mixing, whereas the blend prepared by the two-step mixing showed lower values in both unreacted MA and gel content. On the other hand, the impact energy of the blend prepared by one-step mixing was slightly higher than that of the blend prepared by two-step mixing. This is due to the decreased molecular weight of NR in the formerly prepared MNR of the two-step mixing. For the effect of MA loading, the decrease of unreacted MA content, gel content and rubber particle size were found at low concentration of MA.

• Periodical: Advanced Materials Research (Volume 747)
• Pages: 607-610
• DOI: https://doi.org/10.4028/www.scientific.net/AMR.747.607
• Online since: August 2013
• Authors: Saravalee Saengthaveep, Sadhan C. Jana, Rathanawan Magaraphan
• Keywords: Impact Property, Morpholoy, Natural Rubber (NR), Polystyrene

References

[1] M.N. Ichazo, C. Albano, M. Hernández, J. González, J. Peña, Characterization of Natural Rubber/Cassava Starch/Maleated Natural Rubber Formulations, Rev. LatinAm. Metal. Mat. 31 (2011) 71-84.

[2] S. Horiuchi, N. Matchariyakul, K. Yase, T. Kitano, Morphology Development Through An Interfacial Reaction In Ternary Immiscible Polymer Blends, Macromolecules 30 (1997) 3664-3670.

DOI: 10.1021/ma9615258

[3] L. Zhang, Y. Zhang, H. Yao, Functionalization of Ethylene–Propylene–Diene Monomer Rubber with Maleic Anhydride in the Melt State Through High-Shear Stress-Induced Initiation, J. App. Polym. Sci. 113 (2009) 784–792.

DOI: 10.1002/app.29439